PA6 B3S BASF MALAYSIA
Ultramid®
Thin walled components、parts、Shell、parts、Shell、Thin walled components
crystallization、High mobility、Fast forming cycle、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF MALAYSIA/B3S |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.0 kJ/m² |
| -30°C | ISO 179 | 3.0 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 200 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 250 kJ/m² |
| hardness | Test Condition | Test Method | BASF MALAYSIA/B3S |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 160 Mpa |
| Electrical performance | Test Condition | Test Method | BASF MALAYSIA/B3S |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric constant | 1MHz | IEC 60250 | 3.30 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.030 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | BASF MALAYSIA/B3S |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2 | 90.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.0 % |
| Flexural modulus | 23°C | ISO 178 | 3000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 3400 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 10 % |
| physical property | Test Condition | Test Method | BASF MALAYSIA/B3S |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 3.0 % |
| 饱和,23°C | ISO 62 | 9.5 % | |
| Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 175 cm3/10min |
| density | ISO 1183 | 1.13 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF MALAYSIA/B3S |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C |
| melting temperature | ISO 3146 | 220 °C |