POM 500T NC010 POM vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

POM DUPONT USA 500T NC010

Injection grade

US$ 5,140 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	DUPONT USA/500T NC010
Tensile creep modulus	1hr	ISO 899-1	2300 Mpa
Tensile modulus		ISO 527-2	2300 Mpa
Nominal tensile fracture strain		ISO 527-2	35 %
Bending modulus		ISO 178	2100 Mpa
Tensile creep modulus	1000hr	ISO 899-1	1200 Mpa
Friction coefficient	vs.Itself-Dynamic,1hr	ASTM D1894	0.22
bending strength	3.5%Strain	ISO 178	60.0 Mpa
Tensile strain	Yield	ISO 527-2	18 %
tensile strength	Yield	ISO 527-2	56.0 Mpa
Supplementary Information	Test Condition	Test Method	DUPONT USA/500T NC010
SpecificWear-Against		ASTM D1894	40.0 10^-6mm³/N·m
EmissionofOrganicCompounds		VDA277	3.40 µgC/g
Emission		VDA275	<8.00 mg/kg
thermal performance	Test Condition	Test Method	DUPONT USA/500T NC010
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	78.0 °C
Melting temperature		ISO 11357-3	178 °C
Vicat softening temperature	--	ISO 306/B50	140 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.3E-04 cm/cm/°C
Vicat softening temperature	--	ISO 306/A50	172 °C
AnnealingTime-Optional			30.0 min/mm
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	146 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04 cm/cm/°C
AnnealingTemperature			160 °C
flammability	Test Condition	Test Method	DUPONT USA/500T NC010
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
UL flame retardant rating		1.5mm	UL 94	HB
Fogging-G-value	condensate	ISO 6452	2E-04 g
UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB
UL flame retardant rating		0.75mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	45 mm/min
FMVSS flammability		FMVSS302	B
Physical properties	Test Condition	Test Method	DUPONT USA/500T NC010
density		ISO 1183	1.38 g/cm³
Shrinkage rate	MD	ISO 294-4	1.7 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.82 %
Shrinkage rate	TD	ISO 294-4	1.6 %
MediumDensity			1.18 g/cm³
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.21 %
melt mass-flow rate		ISO 1133	12 g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	10.0 cm3/10min
impact performance	Test Condition	Test Method	DUPONT USA/500T NC010
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	330 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	14 kJ/m²
Impact strength of cantilever beam gap		-40°C	ISO 180/1A	9.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	23°C	ISO 179/1eA	14 kJ/m²
hardness	Test Condition	Test Method	DUPONT USA/500T NC010
Rockwell hardness	M-Sale	ISO 2039-2	79
Rockwell hardness		R-Sale	ISO 2039-2	117
Electrical performance	Test Condition	Test Method	DUPONT USA/500T NC010
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Relative permittivity	100Hz	IEC 60250	3.60
Surface resistivity		IEC 60093	1E+15 ohms
Relative permittivity	1MHz	IEC 60250	3.60
Compared to the anti leakage trace index		IEC 60112	PLC 0