PA66/F/PTFE RFL-4033 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Electronic and Electrical
wear resistant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | 23°C | ISO180/1A | 6.7 kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 35 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 2.10 J | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 7.60 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 3.1 % |
| Flexural modulus | ASTMD790 | 5520 Mpa | |
| Tensile stress | 屈服 | ISO527-2 | 118 Mpa |
| Bending stress | ISO178 | 183 Mpa | |
| Dynamic | ASTMD3702Modified | 0.40 | |
| Tensile modulus | ASTMD638 | 6890 Mpa | |
| bending strength | ASTMD790 | 179 Mpa | |
| Tensile strain | 断裂 | ISO527-2 | 3.1 % |
| Static | ASTMD3702Modified | 0.45 | |
| Tensile stress | 断裂 | ISO527-2 | 118 Mpa |
| elongation | 屈服 | ASTMD638 | 3.1 % |
| Tensile modulus | ISO527-2/1 | 6440 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 120 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 3.1 % |
| tensile strength | 断裂 | ASTMD638 | 120 Mpa |
| Flexural modulus | ISO178 | 5800 Mpa | |
| Wear factor - Washer | ASTMD3702Modified | 19.5 10^-10in^5-min/ft-lb-hr |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Shrinkage rate | TD：24hr | ASTMD955 | 1.6to1.8 % |
| MD:24小时 | ISO294-4 | 0.64 % | |
| TD:24小时 | ISO294-4 | 1.7 % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.60 % |
| Shrinkage rate | MD：24小时 | ASTMD955 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 247 °C | |
| Hot deformation temperature 4 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 260 °C |
| MD：-40到40°C | ISO11359-2 | 8.3E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 3.9E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 8.3E-05 cm/cm/°C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 261 °C | |
| Hot deformation temperature 4 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 243 °C |
| TD：-40到40°C | ASTME831 | 4E-05 cm/cm/°C |