PA66 CM3006G-30-BK TORAY JAPAN
Amilan®
Automotive sector、Electrical components
Thermal stability、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/CM3006G-30-BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 15 kJ/m² |
| -40°C | ISO 179 | 12 kJ/m² | |
| Impact strength of simply supported beam without notch | -40°C | ISO 179 | 85 kJ/m² |
| 23°C | ISO 179 | 90 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/CM3006G-30-BK |
|---|---|---|---|
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 121 |
| M 计秤, 23°C | ISO 2039-2 | 103 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM3006G-30-BK |
|---|---|---|---|
| Tensile strain | 断裂, 80°C | ISO 527-2 | 5.5 % |
| bending strength | -40°C | ISO 178 | 380 Mpa |
| tensile strength | 80°C | ISO 527-2 | 140 Mpa |
| compression stress | -40°C | ISO 604 | 265 Mpa |
| bending strength | 80°C | ISO 178 | 230 Mpa |
| compression stress | 23°C | ISO 604 | 195 Mpa |
| 80°C | ISO 604 | 120 Mpa | |
| Flexural modulus | 80°C | ISO 178 | 8600 Mpa |
| Tensile strain | 断裂, -40°C | ISO 527-2 | 2.5 % |
| 断裂, 23°C | ISO 527-2 | 3.0 % | |
| bending strength | 23°C | ISO 178 | 345 Mpa |
| shear strength | 23°C | ASTM D732 | 105 Mpa |
| Flexural modulus | -40°C | ISO 178 | 15500 Mpa |
| tensile strength | -40°C | ISO 527-2 | 280 Mpa |
| Flexural modulus | 23°C | ISO 178 | 13800 Mpa |
| tensile strength | 23°C | ISO 527-2 | 220 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM3006G-30-BK |
|---|---|---|---|
| dielectric constant | 23°C, 1 kHz | IEC 60250 | 4.50 |
| Dissipation Factor | 23°C, 1 MHz | IEC 60250 | 0.020 |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| dielectric constant | 23°C, 50 Hz | IEC 60250 | 4.70 |
| Volume resistivity | IEC 60093 | 1.0E+13 ohms·cm | |
| Dissipation Factor | 23°C, 1 kHz | IEC 60250 | 0.020 |
| 23°C, 50 Hz | IEC 60250 | 0.020 | |
| dielectric constant | 23°C, 1 MHz | IEC 60250 | 4.10 |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM3006G-30-BK |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.50 g/cm³ |
| Shrinkage rate | 流量 : 3.00 mm | 内部方法 | 0.20 - 0.40 % |
| 横向流量 : 3.00 mm | 内部方法 | 0.50 - 0.80 % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.40 % |
| 饱和, 23°C | ISO 62 | 4.8 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM3006G-30-BK |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 263 °C |
| thermal conductivity | 0.42 W/m/K | ||
| melting temperature | DSC | 265 °C | |
| specific heat | 1500 J/kg/°C | ||
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.0E-5 - 3.0E-5 cm/cm/°C |