PS 8930 PMC GROUP USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PMC GROUP USA/8930 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256A | 130 J/m |
| hardness | Test Condition | Test Method | PMC GROUP USA/8930 |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 55 |
| Mechanical properties | Test Condition | Test Method | PMC GROUP USA/8930 |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 60 % |
| tensile strength | 断裂 | ASTM D638 | 21.0 MPa |
| Flexural modulus | ASTM D790 | 2140 MPa | |
| tensile strength | 屈服 | ASTM D638 | 25.0 MPa |
| flammability | Test Condition | Test Method | PMC GROUP USA/8930 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | PMC GROUP USA/8930 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30to0.60 % |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 10 g/10min |
| Water absorption rate | 饱和,23°C | ASTM D570 | <0.15 % |
| 平衡,23°C,50% | ASTM D570 | <0.10 % | |
| density | ASTM D792 | 1.07 g/cm³ |
| Thermal performance | Test Condition | Test Method | PMC GROUP USA/8930 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 87.0 °C |
| vicat | ASTM D1525 | 100 °C |