Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 100-322 TORAY MALAYSIA
Toyolac®
household electrical appl、Electronic and electrical
Glass fiber reinforced、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY MALAYSIA/100-322 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 0°C,3.20mm | ASTM D256 | 200 J/m |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of cantilever beam gap | -30°C,12.7mm | ASTM D256 | 120 J/m |
| 23°C,3.20mm | ASTM D256 | 270 J/m | |
| 0°C,12.7mm | ASTM D256 | 180 J/m | |
| 23°C,12.7mm | ASTM D256 | 230 J/m | |
| -30°C,3.20mm | ASTM D256 | 140 J/m |
| hardness | Test Condition | Test Method | TORAY MALAYSIA/100-322 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | TORAY MALAYSIA/100-322 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2600 Mpa | |
| fracture | ISO 527-2/50 | >10 % | |
| yield | ASTM D638 | 48.0 Mpa | |
| fracture | ASTM D638 | 48 % | |
| --4 | ASTM D790 | 74.0 Mpa | |
| yield | ISO 527-2/50 | 51.0 Mpa | |
| --5 | ISO 178 | 78.0 Mpa | |
| Flexural modulus | ASTM D790 | 2280 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY MALAYSIA/100-322 |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | 6.6E-03 |
| Surface Resistivity | ASTM D257 | >1.0E+16 ohms | |
| dielectric constant | 1kHz | ASTM D150 | 3.10 |
| Volume resistivity | 23°C | ASTM D257 | >1.0E+16 ohms·cm |
| dielectric strength | ASTM D149 | 23 KV/mm |
| flammability | Test Condition | Test Method | TORAY MALAYSIA/100-322 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY MALAYSIA/100-322 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| density | ASTMD792 | 1.04 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.30 % |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY MALAYSIA/100-322 |
|---|---|---|---|
| thermal conductivity | ASTMC177 | 0.15 W/m/K | |
| 1.8MPa, Unanealed, 12.7mm | ASTM D648 | 93.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.4E-05 cm/cm/°C |
| 1.8MPa, Not annealed | ISO 75-2/A | 83.0 °C | |
| 1.8MPa, Unanealed, 6.40mm | ASTM D648 | 88.0 °C |