PP Homopolymer Generic PP Homopolymer - Mica Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Generic/Generic PP Homopolymer - Mica |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 26to54 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 93to420 J/m |
| hardness | Test Condition | Test Method | Generic/Generic PP Homopolymer - Mica |
|---|---|---|---|
| Rockwell hardness | 23°C | ASTM D785 | 35to113 |
| Mechanical properties | Test Condition | Test Method | Generic/Generic PP Homopolymer - Mica |
|---|---|---|---|
| tensile strength | 断裂,23°C | ASTM D638 | 26.9to31.1 MPa |
| bending strength | 23°C | ASTM D790 | 35.9to55.9 MPa |
| tensile strength | 23°C | ASTM D638 | 29.6to35.4 MPa |
| Tensile modulus | 23°C | ASTM D638 | 1800to4140 MPa |
| Flexural modulus | 23°C | ASTM D790 | 1720to5340 MPa |
| elongation | 屈服,23°C | ASTM D638 | 2.9to7.1 % |
| tensile strength | 屈服,23°C | ASTM D638 | 30.9to37.2 MPa |
| elongation | 断裂,23°C | ASTM D638 | 3.0to20 % |
| physical property | Test Condition | Test Method | Generic/Generic PP Homopolymer - Mica |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.65to1.3 % |
| MD:23°C | ASTM D955 | 0.50to1.3 % | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 2.0to18 g/10min |
| density | ASTM D792 | 0.971to1.25 g/cm³ |
| Thermal performance | Test Condition | Test Method | Generic/Generic PP Homopolymer - Mica |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 57.2to91.7 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 112to138 °C |