PA66 A3WG3 00564 BASF GERMANY
Ultramid®
Laptop case,Industrial machinery,Shell
High mobility,heat-resisting,Filler: Glass fiber reinf,15% filler by weight,15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3WG3 00564 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 200 Mpa |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| 23°C | ISO 179/1eA | 8.0 kJ/m² | |
| Flexural modulus | 23°C | ISO 178 | 5500 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 6000 Mpa |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 43 kJ/m² |
| elongation at break | 23°C | ISO 527-2 | 3.00 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 130 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/A3WG3 00564 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 450 V |
| dielectric strength | IEC 60243-1 | 12 KV/mm | |
| dielectric constant | 23°C | IEC 60250 | 3.50 1MHz |
| Dissipation Factor | 23°C | IEC 60250 | 0.014 1MHz |
| Volume resistivity | IEC 60093 | 1E+10 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | BASF GERMANY/A3WG3 00564 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm | |
| UL -94 | HB 3.00mm | ||
| UL -94 | HB 0.75mm |
| physical property | Test Condition | Test Method | BASF GERMANY/A3WG3 00564 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 7.00 % |
| Shrinkage rate | MD2.0mm | ISO 294-4 | 0.75 % |
| melt mass-flow rate | 275℃/5.0Kg | ISO 1133 | 60 cm3/10min |
| density | ISO 1183 | 1.23 g/cm³ | |
| Water absorption rate | (23°C,50RH) | ISO 62 | 2.20 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/A3WG3 00564 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 240 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3.0E-5 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 250 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7.0E-5 cm/cm/°C |