Product Name
Brand Name
Usages
Properties
Certificates
PA46 TW275F6 DSM HOLAND
Stanyl®
Automotive Applications、Home appliance components
wear resistant、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/TW275F6 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 75 kJ/m² |
| -30°C | ISO 179/1eU | 60 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/TW275F6 |
|---|---|---|---|
| Tensile strain | 断裂, 200°C | ISO 527-2 | 9.4 % |
| Tensile stress | 断裂 | ISO 527-2 | 205 Mpa |
| Tensile strain | 断裂, 180°C | ISO 527-2 | 9.1 % |
| Tensile stress | 断裂, 180°C | ISO 527-2 | 95.0 Mpa |
| 断裂, 200°C | ISO 527-2 | 90.0 Mpa | |
| Tensile strain | 断裂, 120°C | ISO 527-2 | 8.4 % |
| Tensile stress | 断裂, 120°C | ISO 527-2 | 110 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| Flexural modulus | ISO 178 | 9000 Mpa | |
| Tensile strain | 断裂, 160°C | ISO 527-2 | 8.9 % |
| Tensile stress | 断裂, 160°C | ISO 527-2 | 100 Mpa |
| physical property | Test Condition | Test Method | DSM HOLAND/TW275F6 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.5 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.50 % |
| 横向流量 | ISO 294-4 | 1.3 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/TW275F6 |
|---|---|---|---|
| 流动 | ISO 11359-2 | 2.5E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 6.0E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 290 °C |
| Melting temperature 2 | ISO 11357-3 | 295 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 285 °C |