Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC Hylex® P1003L ENTEC USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ENTEC USA/Hylex® P1003L |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | 67 kJ/m² |
| hardness | Test Condition | Test Method | ENTEC USA/Hylex® P1003L |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 120 |
| Mechanical properties | Test Condition | Test Method | ENTEC USA/Hylex® P1003L |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 70.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 120 % |
| Flexural modulus | ISO 178 | 1970 MPa | |
| bending strength | ISO 178 | 88.0 MPa |
| physical property | Test Condition | Test Method | ENTEC USA/Hylex® P1003L |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| Shrinkage rate | MD：3.18mm | ISO 294-4 | 0.50to0.70 % |
| density | ISO 1183 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 3.0 g/10min |
| Thermal performance | Test Condition | Test Method | ENTEC USA/Hylex® P1003L |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 148 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 138 °C |