Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MVLDPE FPS317-A NOVA CANADA
SURPASS®
Laminate,Stretch winding,cast film ,cast film ,Laminate,Stretch winding
low density,Anti perforation,antioxidant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | NOVA CANADA/FPS317-A |
|---|---|---|---|
| elongation at break | 20.0µm | 内部方法 | 360 % |
| LowFrictionPuncture-CastFilm | 20.0µm | 内部方法 | 830 J/cm |
| film | Test Condition | Test Method | NOVA CANADA/FPS317-A |
|---|---|---|---|
| Secant modulus -1% Decant, MD | 20µm,CastFilm | ASTM D882 | 100 Mpa |
| tensile strength | Break,20µm,CastFilm | ASTM D882 | 25.0 Mpa |
| Tensile strain | Break,20µm,CastFilm，MD | ASTM D882 | 470 % |
| Elmendorf tear strength | 20µm,CastFilm，MD | ASTM D1922 | 380 g |
| film thickness | 20 µm | ||
| tensile strength | Yield,20µm,CastFilm | ASTM D882 | 7.00 Mpa |
| Tensile strain | Break,20µm,CastFilm | ASTM D882 | 780 % |
| Elmendorf tear strength | 20µm,CastFilm，TD | ASTM D1922 | 540 g |
| Secant modulus -1% Decant, TD | 20µm,CastFilm | ASTM D882 | 120 Mpa |
| optical performance | Test Condition | Test Method | NOVA CANADA/FPS317-A |
|---|---|---|---|
| gloss | 45°,20.0µm,铸造薄膜 | ASTM D2457 | 85 |
| Haze ratio | 20.0µm,铸造薄膜 | ASTM D1003 | 0.80 % |
| physical property | Test Condition | Test Method | NOVA CANADA/FPS317-A |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 4.0 g/10min |