Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5010GT30 MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Bottle cap,Fitness equipment,Automotive sector,Electronic field,Electrical field
Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT30 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.E+15 Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.E+14 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT30 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 190 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 8600 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 9000 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT30 |
|---|---|---|---|
| purpose | 30%玻纤增强.抗冲击韧性 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT30 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.2 % | |
| density | ASTM D792/ISO 1183 | 1.51 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 9 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.08 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT30 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 210 ℃（℉） |
| melting temperature | 224 ℃（℉） |