Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO SE100X GN3302 SABIC INNOVATIVE SHANGHAI
NORYL™
Electronic communication 、Electronic communication
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SE100X GN3302 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 91 J/m |
| 23°C | ASTM D256 | 260 J/m | |
| Dart impact | -30°C,EnergyatPeakLoad | ASTM D3763 | 16.3 J |
| 23°C,EnergyatPeakLoad | ASTM D3763 | 40.7 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SE100X GN3302 |
|---|---|---|---|
| Flexural modulus | 100mmSpan | ASTM D790 | 2310 Mpa |
| elongation | 断裂 | ASTM D638 | 25 % |
| bending strength | Yield,100mmSpan | ASTM D790 | 82.7 Mpa |
| elongation | 屈服 | ASTM D638 | 6.5 % |
| tensile strength | 断裂 | ASTM D638 | 46.9 Mpa |
| 屈服 | ASTM D638 | 57.9 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SE100X GN3302 |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 6E-03 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| Dissipation Factor | 60Hz | ASTM D150 | 6E-03 |
| dielectric constant | 60Hz | ASTM D150 | 2.66 |
| Volume resistivity | ASTM D257 | 3.1E+16 ohms·cm | |
| dielectric constant | 50Hz | ASTM D150 | 2.66 |
| dielectric strength | 3.20mm,inOil | ASTM D149 | 18 KV/mm |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | ASTM D150 | 2.6E-03 |
| dielectric constant | 1MHz | ASTM D150 | 2.57 |
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SE100X GN3302 |
|---|---|---|---|
| Radiation board grade | UL | YES | |
| UL flame retardant rating | 6.0mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-1 | |
| Limiting Oxygen Index | ASTM D2863 | 33 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SE100X GN3302 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| TD2 | 内部方法 | 0.50-0.70 % | |
| Outdoor applicability | UL 746C | f1 | |
| density | ASTM D792 | 1.10 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/SE100X GN3302 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 92.8 °C |
| 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 102 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI Str | UL 746 | 95.0 °C | |
| RTI Elec | UL 746 | 95.0 °C |