PC/PBT LW5303F LG CHEM KOREA
LUPOX®
household electrical appliances,Electrical applications,Automotive Applications,Electrical/Electronic Applications,switch,Application in the automotive field
Low warpage,Glass fiber reinforced,Flame retardant,Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/LW5303F |
|---|---|---|---|
| tensile strength | Break,3.20mm | ASTM D638 | 132 Mpa |
| elongation | 断裂,3.20mm | ASTM D638 | 2.0 % |
| Flexural modulus | 3.20mm | ASTM D790 | 8830 Mpa |
| bending strength | 3.20mm | ASTM D790 | 186 Mpa |
| flammability | Test Condition | Test Method | LG CHEM KOREA/LW5303F |
|---|---|---|---|
| UL flame retardant rating | 0.70mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LG CHEM KOREA/LW5303F |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.30-0.90 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.080 % |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 6.0 g/10min |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/LW5303F |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 190 °C |
| melting temperature | ASTM D3418 | 223 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C |