Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS SAXALAC™ 420HI SAX AUSTRIA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SAX AUSTRIA/SAXALAC™ 420HI |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 9.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 40 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180 | 40 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 42 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SAX AUSTRIA/SAXALAC™ 420HI |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 15 % |
| Tensile modulus | 23°C | ISO 527-2 | 2300 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 40.0 MPa |
| flammability | Test Condition | Test Method | SAX AUSTRIA/SAXALAC™ 420HI |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | V-0 |
| Burning wire flammability index | IEC 60695-2-12 | 750 °C |
| physical property | Test Condition | Test Method | SAX AUSTRIA/SAXALAC™ 420HI |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 50.0 cm³/10min |
| density | 1.20 g/cm³ | ||
| water content | 内部方法 | <0.20 % | |
| Melt volume flow rate | 收缩率 | ISO 1133 | 0.40to0.70 % |
| 220°C/5.0kg | ISO 1133 | 6.00 cm³/10min |
| Thermal performance | Test Condition | Test Method | SAX AUSTRIA/SAXALAC™ 420HI |
|---|---|---|---|
| ball-indentation hardness | 80°C,2.00mm | IEC 60335-1 | 通过 |
| vicat | ISO 306/B50 | 93.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,60.0mm跨距，HDT | ISO 75-2/A | 82.0 °C |