Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PPA HTNFR52G30NH DUPONT JAPAN

Zytel®

Electronic communication accessories,Electronic communication accessories

enhance,Glass fiber reinforced,Thermal stability,Flame retardant,High temperature resistan

Plastic Datasheets

Supplementary Information	Test Condition	Test Method	DUPONT JAPAN/HTNFR52G30NH
Odor		VDA270	3.50

thermal performance	Test Condition	Test Method	DUPONT JAPAN/HTNFR52G30NH
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	283 °C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	6E-05 cm/cm/°C
		MD：--	ISO 11359-2	2E-05 cm/cm/°C
		MD：-40to23°C	ISO 11359-2	2E-05 cm/cm/°C
		MD：55to160°C	ISO 11359-2	2E-05 cm/cm/°C
		TD：--	ISO 11359-2	6E-05 cm/cm/°C
		TD：55to160°C	ISO 11359-2	1E-04 cm/cm/°C
Melting temperature		ISO 11357-3	310 °C
RTI Elec	0.75mm	UL 746	140 °C
		1.5mm	UL 746	140 °C
		3.0mm	UL 746	140 °C
		0.40mm	UL 746	140 °C

mechanical properties	Test Condition	Test Method	DUPONT JAPAN/HTNFR52G30NH
Bending modulus		ISO 178	9000 Mpa
bending strength		ISO 178	230 Mpa
Tensile modulus		ISO 527-2	10500 Mpa
Tensile strain	Break	ISO 527-2	2.2 %
tensile strength	Break	ISO 527-2	150 Mpa

Electrical performance	Test Condition	Test Method	DUPONT JAPAN/HTNFR52G30NH
Compared to the anti leakage trace index		IEC 60112	V
Dielectric strength		IEC 60243-1	36 KV/mm
Dissipation factor	1MHz	IEC 60250	0.012
Dissipation factor		100Hz	IEC 60250	6.5E-03
Relative permittivity	100Hz	IEC 60250	4.10
Relative permittivity		1MHz	IEC 60250	3.90
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	DUPONT JAPAN/HTNFR52G30NH
Shrinkage rate	MD	ISO 294-4	0.30 %
Shrinkage rate		TD	ISO 294-4	1.0 %

impact performance	Test Condition	Test Method	DUPONT JAPAN/HTNFR52G30NH
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	45 kJ/m²

flammability	Test Condition	Test Method	DUPONT JAPAN/HTNFR52G30NH
Extreme Oxygen Index		ISO 4589-2	37 %
FMVSS flammability		FMVSS302	DNI
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	800 °C
		0.40mm	IEC 60695-2-13	700 °C
		0.75mm	IEC 60695-2-13	725 °C
UL flame retardant rating	0.75mm	UL 94	V-0
		0.75mm	IEC 60695-11-10,-20	V-0
		1.5mm	IEC 60695-11-10,-20	V-0
		1.5mm	UL 94	V-0