TPV 8201-70 CELANESE USA
Santoprene™
Kitchen utensils、Home appliance components、Fatigue relief supplies、Soft handle、Smart phone、Monitor
Low friction coefficient、Low mold expansion、Recyclable materials、Controllable mold expansi、Cleanable、Good melt strength、Good colorability、Ozone resistance、Chemical resistance、Low water absorption、Not absorbing water
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodCELANESE USA/8201-70
Shore hardness邵氏A,15秒,23°C,2.00mmISO 86875
Electrical performanceTest ConditionTest MethodCELANESE USA/8201-70
High arc combustion index (HAI)HAIUL 746PLC 0
Hot wire ignition (HWI)1.60mmUL 746PLC 3
3.00mmUL 746PLC 2
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 0
High Voltage Arc Traceability Rate (HVTR)PLCUL 746
flammabilityTest ConditionTest MethodCELANESE USA/8201-70
UL flame retardant rating3.00mmUL 94HB
1.10mmUL 94HB
1.60mmUL 94HB
elastomerTest ConditionTest MethodCELANESE USA/8201-70
elongation断裂,23°C，横向ASTMD412570 %
125°C,70hrISO 81557 %
tensile strength 断裂,23°C，横向流量ASTMD4127.50 Mpa
23°CASTM D62426.0 kN/m
ISO 34-126 kN/m
70°C,22hrASTM D395B36 %
Tensile stress100%应变,23°C，横向流量ASTMD4122.90 Mpa
125°C,70hrASTM D395B57 %
70°C,22hrISO 81536 %
agingTest ConditionTest MethodCELANESE USA/8201-70
mass change fraction23.0°C,168hr,在IRM903油中ISO 181748 %
23.0°C,168hr,在50%氢氧化钠中ISO 18170.0 %
support A,23 ° C,168hr, exist IRM903 In oilASTM D471-14
Change rate of tensile strength in air150°C,168hrASTMD573-9.0 %
23°C,168hr,在水中ASTMD471-6.0 %
23°C,168hr,在15％氯化钠中ASTMD471-1.0 %
mass change fraction23.0°C,168hr,在15％氯化钠中ISO 18170.0 %
Change rate of ultimate elongation in air23°C,168hr,在15％氯化钠中ASTMD471-2.0 %
mass change fraction23°C,168hr,在IRM903油中ASTM D47148 %
Changes in air quality150°C,168hrASTM D573-9.0 %
mass change fraction23°C,168hr,在15％氯化钠中ASTM D4710.0 %
23.0°C,168hr,在水中ISO 18170.0 %
Change rate of ultimate elongation in air150°C,168hrASTMD573-8.0 %
Change rate of tensile strength in air23°C,168hr,在98％硫酸中ASTMD4713.0 %
support A,23 ° C,168hr, in the waterASTMD471-1.0
support A,23 ° C,168hr, In 98% sulfuric acidISO 1817-1.0
mass change fraction23.0°C,168hr,在98％硫酸中ISO 18171.0 %
Support A, 23 ° C, 168hr, in 50% sodium hydroxideISO 18171.0
Change rate of tensile strength in air23°C,168hr,在IRM903油中ASTMD471-14 %
23°C,168hr,在50%氢氧化钠中ASTMD471-1.0 %
Change rate of ultimate elongation in air23°C,168hr,在水中ASTMD4718.0 %
Changes in air quality150°C,168hrISO 188-9.0 %
Change rate of ultimate elongation in air23°C,168hr,在50%氢氧化钠中ASTMD4712.0 %
Support A, 23 ° C, 168hr, in 50% sodium hydroxideASTM D4711.0
Support A, 23 ° C, 168hr, in 15% sodium chlorideISO 18171.0
mass change fraction23°C,168hr,在98％硫酸中ASTM D4711.0 %
support A,23 ° C,168hr, exist IRM903 In oilISO 1817-14
Change rate of hardness (Shore) in the air支撐A,150°C,168hrASTMD5732.0
support A,23 ° C,168hr, In 98% sulfuric acidASTM D471-1.0
mass change fraction23°C,168hr,在水中ASTM D4710.0 %
Change rate of ultimate elongation in air23°C,168hr,在IRM903油中ASTMD471-14 %
23°C,168hr,在98％硫酸中ASTMD4714.0 %
Support A, 23 ° C, 168hr, in 15% sodium chlorideASTM D4711.0
mass change fraction23°C,168hr,在50%氢氧化钠中ASTM D4710.0 %
Thermal performanceTest ConditionTest MethodCELANESE USA/8201-70
RTI3.00mmUL 74695.0 °C
brittle temperatureASTMD746-63.0 °C
RTI1.10mmUL 74690.0 °C
RTI ElecUL 746100 °C
RTI1.60mmUL 74690.0 °C