PA612 159L DUPONT USA
Zytel®
Engineering accessories、Automotive Applications、Engine parts
Mineral reinforcement、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | DUPONT USA/159L |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 5 kg·cm/cm(J/M)ft·lb/in | |
| Tensile stress | 屈服 | ISO 527-1/2 | 50%RH｜52 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 2150 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | -30℃ | ISO 179/1eA | 50%RH｜4 kJ/m² |
| tensile strength | ASTM D412/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eU | 50%RH｜NB kJ/m² |
| Tensile modulus | 1mm/min | ISO 527-1/2 | 50%RH｜1550 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 50%RH｜6 kJ/m² |
| elongation | ASTM D412/ISO 527 | 4.5 % | |
| Impact strength of simply supported beam without notch | -30℃ | ISO 179/1eU | 50%RH｜NB kJ/m² |
| Tensile strain | 50mm/min，屈服 | ISO 527-1/2 | 50%RH｜19 % |
| elongation at break | 50mm/min，屈服 | ISO 527-1/2 | 50%RH｜＞50 % |
| Impact strength of cantilever beam gap | -30℃ | ISO 180/1A | 50%RH｜4.3 kJ/m² |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 50%RH｜8 kJ/m² |
| Electrical performance | Test Condition | Test Method | DUPONT USA/159L |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 | ASTM D-831 | 50%RH｜- 10-4/℃ |
| dielectric temperature | 0.45MPa | ISO 75-1/2 | 135 °C |
| Linear coefficient of thermal expansion | 横向 | ASTM E-831 | 50%RH｜- 10-4/℃ |
| dielectric temperature | 1.80MPa | ISO 75-1/2 | 50%RH｜- °C |
| other | Test Condition | Test Method | DUPONT USA/159L |
|---|---|---|---|
| characteristic | PA612无筋.润滑。 |
| Physical properties | Test Condition | Test Method | DUPONT USA/159L |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1060 |
| processability | Test Condition | Test Method | DUPONT USA/159L |
|---|---|---|---|
| Temperature | 50-90 °C |
| Thermal performance | Test Condition | Test Method | DUPONT USA/159L |
|---|---|---|---|
| vicat | 20N | ISO 306 | 50%RH｜- °C |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 62 ℃（℉） |
| Melt Temperature | 10℃/min | ISO 3146C | 50%RH｜- °C |