K(Q)胶 3G46 K(Q)胶 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Reference Price

K(Q)胶 BASF GERMANY 3G46

US$ 3,530 / MT

FOB Guangzhou port, China

optical performance	Test Condition	Test Method	BASF GERMANY/3G46
Refractive index		ISO 489	1.573
turbidity		ASTM D1003	0.20 %
Refractive index		ASTM D542	1.573
transmissivity	550nm	ASTM D1003	91.0 %
impact performance	Test Condition	Test Method	BASF GERMANY/3G46
Impact strength of cantilever beam gap	-30°C	ISO 180/A	2.0 kJ/m²
InstrumentedDartImpact	Totalenergy	ASTM D3763	20.1 J
Impact strength of cantilever beam gap	23°C	ISO 180/A	3.0 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	3.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	32 J/m
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
mechanical properties	Test Condition	Test Method	BASF GERMANY/3G46
elongation	Break	ASTM D638	220 %
tensile strength	Yield,23°C	ASTM D638	25.5 Mpa
Tensile modulus		ISO 527-2	1550 Mpa
Tensile modulus			ASTM D638	1640 Mpa
Bending modulus		ISO 178	1550 Mpa
tensile strength	Yield,23°C	ISO 527-2	27.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	2.0 %
bending strength		ASTM D790	27.2 Mpa
		5.0%Strain		31.0 Mpa
		--	ISO 178	31.0 Mpa
Bending modulus		ASTM D790	1330 Mpa
Nominal tensile fracture strain	23°C	ISO 527-2	180 %
Electrical performance	Test Condition	Test Method	BASF GERMANY/3G46
Dielectric constant	1.00mm,1MHz	ASTM D150	2.50
Dielectric constant		100Hz	IEC 60250	2.50
Surface resistivity		ASTM D257	>1.0E+14 ohms
Dissipation factor	100Hz	IEC 60250	3E-04
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	8E-04
Surface resistivity		IEC 60093	1E+15 ohms
Compared to the anti leakage trace index		IEC 60112	PLC 0
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm
Physical properties	Test Condition	Test Method	BASF GERMANY/3G46
density		ISO 1183	1.02 g/cm³
Melt Volume Flow Rate (MVR)	200°C/5.0kg	ISO 1133	12.0 cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	11 g/10min
Shrinkage rate	MD	ASTM D955	0.65 %
Shrinkage rate			ISO 294-4	0.30-1.0 %
Water absorption rate	Saturation,23°C	ASTM D570	0.070 %
density		ASTM D792	1.02 g/cm³
Water absorption rate	Saturation,23°C	ISO 62	0.070 %
hardness	Test Condition	Test Method	BASF GERMANY/3G46
Shore hardness	ShoreD	ASTM D2240	75
Shore hardness		ShoreD	ISO 868	65
thermal performance	Test Condition	Test Method	BASF GERMANY/3G46
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	75.6 °C
		1.8MPa,Annealed	ISO 75-2/A	58.0 °C
		0.45MPa,Annealed	ISO 75-2/B	75.0 °C
Vicat softening temperature	--	ISO 306/B50	51.0 °C
Vicat softening temperature			ASTM D15253	87.8 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6.0E-5to9.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/A50	81.0 °C
Linear coefficient of thermal expansion	MD	ASTM D696	1.3E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	60.0 °C
film	Test Condition	Test Method	BASF GERMANY/3G46
elongation	Break	ISO 527-3	180 %