PA46 TW241F8 BK DSM HOLAND

Stanyl®

Home appliance components,Electronic and electrical components

Lubricity,Thermal stability

UL

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	DSM HOLAND/TW241F8 BK
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	290 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/A	290 °C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	5.0E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow	ISO 11359-2	2.5E-5 cm/cm/°C
Melting temperature		ISO 11357-3	295 °C
RTI Elec	0.75 mm	UL 746	65.0 °C
Thermal Index - 5000 hr		IEC 60216	177 °C

mechanical properties	Test Condition	Test Method	DSM HOLAND/TW241F8 BK
Bending modulus	--	ISO 178	11500 Mpa
		120°C	ISO 178	5800 Mpa
		160°C	ISO 178	5200 Mpa
Tensile modulus	200°C	ISO 527-2	5300 Mpa
		--	ISO 527-2	13000 Mpa
		120°C	ISO 527-2	6900 Mpa
		160°C	ISO 527-2	6100 Mpa
		180°C	ISO 527-2	5700 Mpa
Tensile strain	Break, 180°C	ISO 527-2	6.5 %
		Break, 160°C	ISO 527-2	6.5 %
		Break, 120°C	ISO 527-2	6.5 %
		Break	ISO 527-2	3.0 %
		Break, 200°C	ISO 527-2	6.5 %
tensile strength	Break, 120°C	ISO 527-2	130 Mpa
		Break, 200°C	ISO 527-2	100 Mpa
		Break	ISO 527-2	230 Mpa
		Break, 180°C	ISO 527-2	105 Mpa
		Break, 160°C	ISO 527-2	115 Mpa

Electrical performance	Test Condition	Test Method	DSM HOLAND/TW241F8 BK
Compared to the anti leakage trace index		IEC 60112	PLC 2
Dielectric strength		IEC 60243-1	30 KV/mm
Relative permittivity	100 Hz	IEC 60250	4.30
Relative permittivity		1 MHz	IEC 60250	4.00
Volume resistivity		IEC 60093	1.0E+14 ohms·cm

Physical properties	Test Condition	Test Method	DSM HOLAND/TW241F8 BK
density		ISO 1183	1.51 g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.1 %
Shrinkage rate		Flow	ISO 294-4	0.50 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.2 %

impact performance	Test Condition	Test Method	DSM HOLAND/TW241F8 BK
Charpy Notched Impact Strength	23°C	ISO 179/1eA	14 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	12 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	12 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	14 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	75 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	95 kJ/m²

flammability	Test Condition	Test Method	DSM HOLAND/TW241F8 BK
Flammability level		UL 94	HB