PLA+ABS LA13A UMG JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UMG JAPAN/LA13A |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 27 kJ/m² |
| hardness | Test Condition | Test Method | UMG JAPAN/LA13A |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 105 |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/LA13A |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 2400 MPa |
| tensile strength | 23°C | ISO 527-2 | 48.0 MPa |
| bending strength | 23°C | ISO 178 | 72.0 MPa |
| physical property | Test Condition | Test Method | UMG JAPAN/LA13A |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.50to0.80 % |
| density | 23°C | ISO 1183 | 1.12 g/cm³ |
| Melt volume flow rate | 200°C/10.0kg | ISO 1133 | 15.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/LA13A |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 92.0 °C |