Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS XCM830-76701 SABIC INNOVATIVE US
CYCOLAC™
Automotive interior parts、Electrical applications
High mobility、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCM830-76701 |
|---|---|---|---|
| Thermal Conductivity | ISO8302 | 0.20 W/m/K | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831,ISO11359-2 | 6E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ASTMD152510,ISO306/B5010 | 138 °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | 通过 |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距9 | ISO75-2/Af | 118 °C |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831,ISO11359-2 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 118 °C |
| Vicat Softening Temperature | -- | ISO306/B120 | 140 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/XCM830-76701 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.10 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.70到0.80 % |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 9.00 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.40 % |
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 11 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCM830-76701 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO527-2/5 | 55.0 Mpa |
| Tensile Modulus | --2 | ASTMD638 | 3400 Mpa |
| Tensile Strength | 断裂3 | ASTMD638 | 55.0 Mpa |
| Flexural Stress | 屈服,50.0mm跨距4 | ASTMD790 | 95.0 Mpa |
| Tensile Elongation | 屈服 | ISO527-2/5 | 5.0 % |
| 断裂3 | ASTMD638 | 100 % | |
| Flexural Stress | --5,6 | ISO178 | 95.0 Mpa |
| Flexural Modulus | 50.0mm跨距4 | ASTMD790 | 3100 Mpa |
| Tensile Strength | 屈服 | ISO527-2/5 | 56.0 Mpa |
| Tensile Elongation | 屈服3 | ASTMD638 | 5.0 % |
| Tensile Modulus | -- | ISO527-2/1 | 3100 Mpa |
| Tensile Strength | 屈服3 | ASTMD638 | 60.0 Mpa |
| Tensile Elongation | 断裂 | ISO527-2/5 | 100 % |
| Flexural Modulus | --5 | ISO178 | 3100 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCM830-76701 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 65.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 45 kJ/m² |