Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PEI UF5011S-1000 SABIC INNOVATIVE US
ULTEM™
household electrical appl、Electrical applications
Aging resistance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/UF5011S-1000 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
Suspended wall beam without notch impact strength | -30°C9 | ISO 180/1U | 无断裂 |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 30.0 J |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2100 J/m |
Reverse notch impact | 3.20mm | ASTM D256 | 2100 J/m |
Suspended wall beam without notch impact strength | 23°C9 | ISO 180/1U | 无断裂 |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/UF5011S-1000 |
---|---|---|---|
tensile strength | 屈服4 | ASTM D638 | 100 Mpa |
断裂 | ISO 527-2/5 | 85.0 Mpa | |
elongation | 断裂4 | ASTM D638 | 60 % |
bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 138 Mpa |
Tensile modulus | --3 | ASTM D638 | 2900 Mpa |
Flexural modulus | 50.0mm跨距5 | ASTM D790 | 3100 Mpa |
bending strength | --6,7 | ISO 178 | 110 Mpa |
Flexural modulus | --6 | ISO 178 | 2900 Mpa |
elongation | 屈服 | ISO 527-2/5 | 8.0 % |
tensile strength | 屈服 | ISO 527-2/5 | 100 Mpa |
elongation | 屈服4 | ASTM D638 | 8.0 % |
tensile strength | 断裂4 | ASTM D638 | 75.0 Mpa |
Tensile modulus | -- | ISO 527-2/1 | 2900 Mpa |
elongation | 断裂 | ISO 527-2/5 | 50 % |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/UF5011S-1000 |
---|---|---|---|
dielectric constant | 60Hz | ASTM D150 | 3.20 |
50Hz | ASTM D150 | 3.20 | |
dielectric strength | 3.20mm,inOil | ASTM D149 | 18 KV/mm |
Volume resistivity | IEC 60093 | 2.5E+15 ohms·cm | |
Dissipation Factor | 60Hz | ASTMD150 | 2.1E-03 |
50Hz | ASTMD150 | 2.1E-03 | |
Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | V |
dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 18 KV/mm |
Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | PLC 4 |
physical property | Test Condition | Test Method | SABIC INNOVATIVE US/UF5011S-1000 |
---|---|---|---|
Melt volume flow rate | 360°C/5.0kg | ISO 1133 | 20.0 cm3/10min |
Shrinkage rate | MD:3.20mm | 内部方法 | 0.40-0.70 % |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
饱和,23°C | ISO 62 | 1.2 % | |
Shrinkage rate | TD:3.20mm | 内部方法 | 0.40-0.70 % |
MD2 | 内部方法 | 0.40-0.70 % | |
melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 11 g/10min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/UF5011S-1000 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,6.40mm,HDT | ASTM D648 | 204 °C |
0.45MPa,未退火,100mm跨距10,HDT | ISO 75-2/Be | 210 °C | |
0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 213 °C | |
1.8MPa,未退火,100mm跨距10,HDT | ISO 75-2/Ae | 200 °C | |
0.45MPa,未退火,6.40mm,HDT | ASTM D648 | 216 °C | |
Linear coefficient of thermal expansion | MD:23到150°C | ISO 11359-2 | 5.5E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距11,HDT | ISO 75-2/Bf | 208 °C |
Linear coefficient of thermal expansion | MD:-40到150°C | ASTME831 | 5.5E-05 cm/cm/°C |
TD:23到150°C | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
vicat | -- | ASTM D152512 | 227 °C |
thermal conductivity | ASTMC177 | 0.31 W/m/K | |
vicat | -- | ISO 306/A50 | 220 °C |
Linear coefficient of thermal expansion | TD:-40到150°C | ASTME831 | 5.5E-05 cm/cm/°C |
vicat | -- | ISO 306/B50 | 215 °C |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 201 °C |
1.8MPa,未退火,64.0mm跨距11,HDT | ISO 75-2/Af | 198 °C | |
ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |