PA+PPO(PPE) XYRON™ AT602 ASAHI JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/XYRON™ AT602 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/XYRON™ AT602 |
|---|---|---|---|
| dielectric constant | 100Hz | IEC 60250 | 3.30 |
| Dissipation Factor | 100Hz | IEC 60250 | 7E-03 |
| Volume resistivity | 23°C | IEC 60093 | 4.5 ohms·cm |
| dielectric strength | 2.00mm | IEC 60243-1 | 27 kV/mm |
| dielectric constant | 1MHz | IEC 60250 | 3.10 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.011 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/XYRON™ AT602 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 3900 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 7.0 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 55.0 MPa |
| bending strength | 23°C | ISO 178 | 95.0 MPa |
| physical property | Test Condition | Test Method | ASAHI JAPAN/XYRON™ AT602 |
|---|---|---|---|
| density | ISO 1183 | 1.25 g/cm³ | |
| Shrinkage rate | 3.00mm | 内部方法 | 1.0to1.3 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/XYRON™ AT602 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-30到65°C | ISO 11359-2 | 5E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 138 °C |