PC LUX7632C-WH8F013X SABIC INNOVATIVE US
LEXAN™ 
Plastic bag、Lighting applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH8F013X
RTIUL 746125 °C
Deflection Temperature Under Load?1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9ISO 75-2/Ae120 °C
Linear thermal expansion coefficient横向 : -40 到 40°CASTM E8317.0E-5 cm/cm/°C
Vicat Softening Temperature--ISO 306/B50137 °C
--ASTM D152510136 °C
--ISO 306/B120139 °C
RTI ElecUL 746125 °C
Linear thermal expansion coefficient流动 : -40 到 40°CASTM E8316.6E-5 cm/cm/°C
横向 : 23 到 80°CISO 11359-27.6E-5 cm/cm/°C
Deflection Temperature Under Load?0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 9ISO 75-2/Be131 °C
Ball PressureTest123 到 127°CIEC 60695-10-2通过
Linear thermal expansion coefficient流动 : 23 到 80°CISO 11359-27.2E-5 cm/cm/°C
RTI ImpUL 746120 °C
Deflection Temperature Under Load?1.8 MPa, 未退火, 3.20 mmASTM D648120 °C
0.45 MPa, 未退火, 3.20 mmASTM D648131 °C
InjectionTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH8F013X
Middle Temperature275 到 300 °C
Drying Time3.0 到 4.0 hr
Suggested Shot Size40 到 60 %
Drying Temperature120 °C
Mold Temperature70 到 95 °C
Vent Depth0.025 到 0.076 mm
Suggested Max Moisture0.020 %
Processing (Melt) Temp290 到 310 °C
Rear Temperature265 到 290 °C
Nozzle Temperature280 到 305 °C
Front Temperature290 到 310 °C
Back Pressure0.300 到 0.700 Mpa
Screw Speed40 到 70 rpm
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH8F013X
Moisture Absorption平衡, 23°C, 50% RHISO 620.11 %
Melt Mass-Flow Rate300°C/1.2 kgASTM D12385.0 g/10 min
Outdoor SuitabilityUL 746Cf1
Modeling Shrinkage横向流动 : 3.20 mm内部方法0.60 到 0.80 %
流动 : 3.20 mm内部方法0.55 到 0.75 %
Moisture Absorption饱和, 23°CISO 620.14 %
Melt Volume flow Rate300°C/1.2 kgISO 11335.00 cm3/10min
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH8F013X
Tensile Strength断裂ISO 527-2/5052.0 Mpa
Tensile Modulus--ISO 527-2/12400 Mpa
Tensile Elongation断裂 3ASTM D63851 %
Tensile Strength屈服 3ASTM D63868.0 Mpa
Tensile Elongation屈服ISO 527-2/506.0 %
Flexural Modulus50.0 mm 跨距 4ASTM D7902400 Mpa
Tensile Modulus-- 2ASTM D6382500 Mpa
Tensile Strength屈服ISO 527-2/5067.0 Mpa
Flexural Stress屈服, 50.0 mm 跨距 4ASTM D790106 Mpa
Tensile Elongation屈服 3ASTM D6386.0 %
Flexural Stress-- 5, 6ISO 178103 Mpa
Flexural Modulus-- 5ISO 1782500 Mpa
Tensile Elongation断裂ISO 527-2/5023 %
Tensile Strength断裂 3ASTM D63852.0 Mpa
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH8F013X
Unnotched Izod Impact Strength23°CASTM D4812, ISO 180/1U无断裂
-30°CASTM D4812, ISO 180/1U无断裂
Instrumented Dart Impact23°C, Total EnergyASTM D376366.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
23°CISO 179/1eA10 kJ/m²
Charpy Unnotched Impact Strength23°CISO 179/1eU无断裂
-30°CISO 179/1eU无断裂
FlammabilityTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH8F013X
UL flame retardant rating1.0 mmUL 94V-0
0.40 mmUL 94V-2
Glow Wire Ignition Temperature1.0 mmIEC 60695-2-13875 °C
UL flame retardant rating3.0 mmUL 945VA
Glow Wire Flammability Index1.0 mmIEC 60695-2-12960 °C
Electrical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH8F013X
Dissipation Factor?1.10 GHzASTM ES7-835.8E-3
Dielectric Constant1.10 GHzASTM ES7-832.79