PC 2805 550207 PC vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PC COVESTRO SHANGHAI 2805 550207

Injection grade

US$ 2,520 / MT

FOB Shanghai port, China

Physical properties	Test Condition	Test Method	COVESTRO SHANGHAI/2805 550207
melt mass-flow rate	250℃；2.16kg	ISO 1133	-- cm3/(10分钟)
Shrinkage rate	60602；500bar，Flow	ISO 294-4	0.65 %
Shrinkage rate		60602；500bar，垂直	ISO 294-4	0.7 %
melt mass-flow rate	300℃；1.2kg	ISO 1133	9.5 cm3/(10分钟)
thermal performance	Test Condition	Test Method	COVESTRO SHANGHAI/2805 550207
UL flame retardant rating	1.5毫米	UL 94	V-2 级
Vicat softening temperature	50N；50℃/hr	ISO 306	145 ℃
UL flame retardant rating	厚度	UL 94	HB(2.5) 级
Extreme Oxygen Index	A溶液	ISO 4589-2	27 %
Linear coefficient of thermal expansion	23-55℃，Flow	ISO 11359-1-2	0.65 10-4/K
Glow wire ignition temperature (GWIT)	3.0毫米	IEC 60695-2-13	875 ℃
Linear coefficient of thermal expansion	23-55℃，垂直	ISO 11359-1-2	0.65 10-4/K
Glow wire combustion index (GWFI)	1.0毫米	IEC 60695-2-12	930 ℃
Glow wire combustion index (GWFI)		1.5毫米	IEC 60695-2-12	850 ℃
Glow wire ignition temperature (GWIT)	1.5毫米	IEC 60695-2-13	875 ℃
Glass transition temperature	10℃/毫米	ISO 11357-1-2	145 ℃
mechanical properties	Test Condition	Test Method	COVESTRO SHANGHAI/2805 550207
Tensile stress	23℃/50%r.h 50毫米/分钟，Yield	ISO 527-1-2	66 MPa
Tensile creep modulus	23℃/50%r.h 1hr	ISO 899-1	2200 MPa
Tensile creep modulus		23℃/50%r.h 1000hr	ISO 899-1	1900 MPa
Tensile strain	23℃/50%r.h 50毫米/分钟，Yield	ISO 527-1-2	6.1 %
Charpy Notched Impact Strength	23℃/50%r.h ；3毫米	kJ/m²	参照ISO 179/1eA 75P(C)
Bending modulus	23℃/50%r.h 2毫米/分钟	ISO 179	2400 MPa
Tensile modulus	23℃/50%r.h 1毫米/分钟	ISO 527-1-2	2400 MPa
tensile strength	23℃/50%r.h，Break	ISO 6603-2	60 J
Maximum destructive power	23℃/50%r.h	ISO 6603-2	5400 N
Elongation at Break	23℃/50%r.h 50毫米/分钟	ISO 527-1-2	＞50 %
Fracture strain	23℃/50%r.h 5毫米/分钟	ISO 527-1-2	-- %
Charpy Notched Impact Strength	23℃/50%r.h	ISO 179/1eU	N kJ/m²
Fracture stress	23℃/50%r.h 5毫米/分钟	ISO 527-1-2	-- MPa
Impact strength of cantilever beam gap	23℃/50%r.h ；3.2毫米	kJ/m²	参照ISO 180/1eA 85P(C)
Electrical performance	Test Condition	Test Method	COVESTRO SHANGHAI/2805 550207
Volume resistivity	23℃/50%r.h	IEC 60093	1E+14 Ohm.m
Dissipation factor	23℃/50%r.h 100Hz	IEC 60250	5 10-4
Dielectric constant	23℃/50%r.h 100Hz	IEC 60250	3.1 --
Dielectric strength	23℃/50%r.h 1毫米	IEC 60243-1	34 kv/毫米
Dissipation factor	23℃/50%r.h 1MHz	IEC 60250	90 10-4
Compared to the Leakage Traceability Index (CTI)	23℃/50%r.h 方法A	IEC 60112	250 等级
Surface resistivity	23℃/50%r.h	IEC 60093	1E+16 Ohm
Dielectric constant	23℃/50%r.h 1MHz	IEC 60250	3.0 --
Specific properties of raw materials	Test Condition	Test Method	COVESTRO SHANGHAI/2805 550207
Transmittance rate	1毫米	ISO 13468-2	89 %
Refractive index	过程A	ISO 489	1.586 --
other	Test Condition	Test Method	COVESTRO SHANGHAI/2805 550207
Water absorption rate	23℃：50%rh，静态均衡值	ISO 62	0.12 %
Water absorption rate		在23℃水中，Saturation值	ISO 62	0.30 %
density	--	ISO 1183	1200 kg/m2