Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA+Olefin NEALID XG370 AD MAJORIS FRANCE
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AD MAJORIS FRANCE/NEALID XG370 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 38 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179 | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | AD MAJORIS FRANCE/NEALID XG370 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10100 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 132 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | ISO 178 | 8900 MPa | |
| bending strength | ISO 178 | 199 MPa |
| Electrical performance | Test Condition | Test Method | AD MAJORIS FRANCE/NEALID XG370 |
|---|---|---|---|
| Surface Resistivity | DIN 53482 | 1E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Volume resistivity | DIN 53482 | 1E+15 ohms·cm |
| flammability | Test Condition | Test Method | AD MAJORIS FRANCE/NEALID XG370 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | AD MAJORIS FRANCE/NEALID XG370 |
|---|---|---|---|
| Shrinkage rate | 0.30to0.70 % | ||
| Water absorption rate | 平衡,23°C,50%RH | 0.90 % | |
| density | ISO 1183 | 1.33 g/cm³ |
| Thermal performance | Test Condition | Test Method | AD MAJORIS FRANCE/NEALID XG370 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 246 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 230 °C | |
| melting temperature | ISO 3146 | 220 °C |