Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS C1110-701 SABIC INNOVATIVE NANSHA
CYCOLOY™
Electrical field、Electronic field、Automotive interior parts
High mobility、High impact resistance、 High flow、High impact、 High flow、High impact
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1110-701 |
|---|---|---|---|
| Rockwell hardness | ASTM D-785 | - R | |
| Tensile modulus | ASTM D-638 | 2205 Mpa | |
| Flexural modulus | ASTM D-790 | 2343 Mpa | |
| bending strength | ASTM D-790 | 86 Mpa | |
| elongation at break | 断裂点 | ASTM D-638 | 150 % |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 640 J/m |
| tensile strength | 屈伏点 | ASTM D-638 | 56 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1110-701 |
|---|---|---|---|
| Dissipation Factor | 1MHz | ASTM D-150 | - |
| dielectric constant | 1MHz | ASTM D-150 | - |
| Volume resistivity | ASTM D-257 | - ohm-cm | |
| Surface Resistivity | ASTM D-257 | - ohm-cm |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1110-701 |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.1 % | |
| density | ASTM D-792 | 1.14 | |
| Shrinkage rate | 3.2mm | ASTM D-955 | 5-7 E-3 |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1110-701 |
|---|---|---|---|
| Linear coefficient of thermal expansion | E831 | 7.2E-05 1/℃ | |
| UL flame retardant rating | UL -94 | 1.5 mm | |
| Heat distortion temperature | 0.45Mpa，HDT | ASTM D-648 | 123 °C |
| Long term use temperature | 无冲击 | UL -746B | 60 °C |
| 含冲击 | UL -746B | 60 °C | |
| vicat | ASTM D-1525 | - °C | |
| Heat distortion temperature | 1.8Mpa，HDT | ASTM D-648 | 107 °C |
| UL flame retardant rating | UL -94 | HB |