Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP Copolymer Retpol® CA 03 UVH 澳大利亚PolyPacific
--
室外应用
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 澳大利亚PolyPacific/Retpol® CA 03 UVH |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 3.00mm | ASTM D256 | 无断裂 |
| Impact strength of cantilever beam gap | 3.00mm | ASTM D256 | 90 J/m |
| hardness | Test Condition | Test Method | 澳大利亚PolyPacific/Retpol® CA 03 UVH |
|---|---|---|---|
| Hardness (Shore) | 邵氏D,3.00mm | ASTM D2240 | 72 |
| 邵氏D,15秒,3.00mm | ASTM D2240 | 62 | |
| Rockwell hardness | R级,3.00mm | ASTM D785 | 82 |
| Mechanical properties | Test Condition | Test Method | 澳大利亚PolyPacific/Retpol® CA 03 UVH |
|---|---|---|---|
| tensile strength | 3.00mm | ASTM D638 | 24.0 MPa |
| elongation | 断裂,3.00mm | ASTM D638 | 500 % |
| Flexural modulus | 3.00mm | ASTM D790 | 1130 MPa |
| physical property | Test Condition | Test Method | 澳大利亚PolyPacific/Retpol® CA 03 UVH |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 1.5to1.9 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 5.0 g/10min |
| density | ASTM D792 | 0.898 g/cm³ |
| Thermal performance | Test Condition | Test Method | 澳大利亚PolyPacific/Retpol® CA 03 UVH |
|---|---|---|---|
| MD：-30到30°C,3.00mm | ASTM D696 | 1E-04 cm/cm/°C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火,3.00mm，HDT | ASTM D648 | 90.0 °C |