PPS A310MB7 TORAY JAPAN
Torelina®
Fiber grade
Flame retardant、Glass fiber reinforced、Mineral reinforcement、High rigidity、high strength、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | TORAY JAPAN/A310MB7 |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.02 % |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A310MB7 |
|---|---|---|---|
| dielectric strength | ASTM D-149 | 15 MV/m | |
| Induced positive connection | 10 | ASTM D-150 | 0.002 |
| Inherent resistance of volume | ASTM D-257 | 10 Ω.m | |
| arc resistance | W电极 | ASTM D-495 | 182 秒 |
| dielectric constant | 10 | ASTM D-150 | 5.8 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A310MB7 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 240(MPa) kg/cm²(MPa)[Lb/in²] | |
| Shore hardness | ASTM D-785 | 123 洛氏 | |
| coefficient of friction | 对钢 | ASTM D-1894 | 0.30 |
| Impact strength of cantilever beam gap | 无缺口23℃ | ASTM D-256 | 20 KJ/m |
| bending strength | ASTM D-790 | 200 Mpa | |
| abrasion | ASTM D-1044 | 70 mg/1000回 | |
| tensile strength | ASTM D-638 | 140 Mpa | |
| limiting pv value | 东丽法 | 815 KJ/m | |
| Rockwell hardness | ASTM D785 | 123 | |
| tensile strength | ASTM D638/ISO 527 | 141(MPa) kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D-790 | 17.6 GPa | |
| Impact strength of cantilever beam gap | 缺口23℃ | ASTM D-256 | 90 J/m |
| elongation at break | ASTM D-732 | 60 | |
| tensile strength | ASTM D-638 | 1.2 % |
| physical property | Test Condition | Test Method | TORAY JAPAN/A310MB7 |
|---|---|---|---|
| Shrinkage rate | 流动方向 | 东丽法 | 0.15 % |
| 320℃,98MPa,1mm厚，流动长 | 东丽法 | 90 | |
| Shrinkage rate | 垂重方向 | 东丽法 | 0.55 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A310MB7 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Linear coefficient of thermal expansion | 垂重方向 | ASTM D-696 | 2.4 |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | >260 °C |
| combustibility | UL -94 | V-0 | |
| Linear coefficient of thermal expansion | 流动方向 | ASTM D-696 | 1.6 |
| melting temperature | DSC | 278 °C | |
| 278 ℃（℉） |