Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 3412ECR-739 SABIC INNOVATIVE NANSHA
LEXAN™ 
Plastic bag、Automotive External Parts、Industrial applications、Electrical appliances、Lighting applications、Medical supplies
Glass fiber reinforced、enhance、Flame retardant、High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
Suspended wall beam without notch impact strength-30°CISO 180/1U35 kJ/m²
23°CISO 180/1U35 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA6.0 kJ/m²
Impact strength of cantilever beam gap-30°CASTM D256110 J/m
23°CASTM D256110 J/m
Dart impact23°C,TotalEnergyASTM D376320.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA5.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU40 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A7.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU40 kJ/m²
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
Tensile modulusISO 527-2/16000 Mpa
tensile strength 断裂ISO 527-2/590.0 Mpa
elongation屈服ASTM D6383.1 %
Tensile strain屈服ISO 527-2/52.8 %
tensile strength 断裂ASTM D63887.0 Mpa
Flexural modulus50.0mm跨距ASTM D7905000 Mpa
tensile strength 屈服ISO 527-2/595.0 Mpa
Tensile modulusASTM D6385500 Mpa
bending strength屈服,50.0mm跨距ASTM D790156 Mpa
ISO 178140 Mpa
Flexural modulusISO 1785500 Mpa
Tensile strain断裂ISO 527-2/53.2 %
tensile strength 屈服ASTM D63890.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
relative permittivity60HzIEC 602503.30
50HzIEC 602503.30
High arc combustion index (HAI)HAIUL 746PLC 3
relative permittivity1MHzIEC 602503.30
Dissipation Factor50HzIEC 602500.020
60HzIEC 602500.020
1MHzIEC 602500.010
High Voltage Arc Traceability Rate (HVTR)HVTRUL 746PLC 3
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Hot wire ignition (HWI)HWIUL 746PLC 0
arc resistanceASTM D495PLC7
Surface ResistivityIEC 60093>1.0E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 3
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
UL flame retardant rating3.0mmUL 945VA
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
UL flame retardant rating1.5mmUL 94V-0
Limiting Oxygen IndexISO 4589-240 %
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
Shrinkage rateMD：3.20mm内部方法0.20-0.50 %
Melt volume flow rate300°C/1.2kgISO 11337.00 cm3/10min
Shrinkage rateTD：3.20mm内部方法0.20-0.50 %
Water absorption rate平衡,23°C,50%RHISO 620.12 %
饱和,23°CISO 620.29 %
densityASTM D7921.30 g/cm³
ISO 11831.36 g/cm³
melt mass-flow rate300°C/1.2kgASTM D12387.0 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
Linear coefficient of thermal expansionMD：-40到40°CASTME8313E-05 cm/cm/°C
vicatASTM D152510147 °C
RTI StrUL 746130 °C
Heat distortion temperature0.45MPa,Unannealed,64.0mmSpan，HDTISO 75-2/Bf141 °C
vicat--ISO 306/B120146 °C
Linear coefficient of thermal expansionTD：-40到40°CASTME8317E-05 cm/cm/°C
vicat--ISO 306/B50145 °C
Heat distortion temperature1.8MPa,Unannealed,64.0mmSpan，HDTISO 75-2/Af136 °C
Linear coefficient of thermal expansionMD：23到80°CISO 11359-23E-05 cm/cm/°C
RTI ImpUL 746130 °C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648141 °C
ball-indentation hardness125°CIEC 60695-10-2Pass
RTI ElecUL 746130 °C