Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC TR1801A SUMITOMO JAPAN
SD POLYCA™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SUMITOMO JAPAN/TR1801A |
|---|---|---|---|
| Charpy Notched Impact Strength | 无缺口无缺口，23℃，5mm | ISO 179-1 | NB kJ/m² |
| 缺口缺口，23℃，4mm | ISO 179-1 | 3 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SUMITOMO JAPAN/TR1801A |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2300 Mpa | |
| bending strength | ISO 178 | 70 Mpa | |
| Tensile strain | 断裂断裂 | ISO 527-2 | 15 % |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 55 Mpa |
| optical performance | Test Condition | Test Method | SUMITOMO JAPAN/TR1801A |
|---|---|---|---|
| Haze ratio | 2 mm2mm | ISO 14782 | 0.3 % |
| Total Light Transmittance | 2mm2mm | ISO 13468 | 90 % |
| refractive index | ISO 489 | 1.582 |
| Flame retardant performance | Test Condition | Test Method | SUMITOMO JAPAN/TR1801A |
|---|---|---|---|
| UL flame retardant rating | 0.35 mm | UL 94 | V-2 |
| 3.00 mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SUMITOMO JAPAN/TR1801A |
|---|---|---|---|
| melt mass-flow rate | 300℃，1.20kg300℃，1.2kg | ISO 1133 | 180 g/10min |
| Melt volume flow rate | 300℃，1.2 kg300℃，1.2kg | ISO 1133 | 171 cm3/10min |
| density | ISO 1183 | 1.2 g/cm³ | |
| Shrinkage rate | MDMD | 内部方法 | 0.5-0.7 % |
| TDTD | 内部方法 | 0.5-0.7 % | |
| Water absorption rate | 23℃，24hr23℃，24hrs | ISO 62 | 0.2 % |
| Thermal performance | Test Condition | Test Method | SUMITOMO JAPAN/TR1801A |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa1.80MPa，HDT | ISO 75/Af | 116 °C |
| Linear coefficient of thermal expansion | TDTD | ISO 11359-2 | 0.000070 cm/cm/℃ |
| MDMD | ISO 11359-2 | 0.000070 cm/cm/℃ |