TPV 211-45 CELANESE USA
Santoprene™
Washer、packing、Automotive sector
dimensional stability 、Low compression deformati、Recyclable materials、Good forming performance、High mobility、Good liquidity、Good colorability、Ozone resistance、Chemical resistance、Fatigue resistance、soft
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CELANESE USA/211-45 |
|---|---|---|---|
| Shore hardness | 邵氏A,15秒,23°C | ISO 868 | 49 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/211-45 |
|---|---|---|---|
| dielectric constant | 23°C,2.03mm | IEC 60250 | 2.40 |
| dielectric strength | 23°C,2.00mm | ASTM D149 | 30 KV/mm |
| dielectric constant | 23°C,2.03mm | ASTM D150 | 2.40 |
| flammability | Test Condition | Test Method | CELANESE USA/211-45 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.0mm | UL 94 | HB |
| elastomer | Test Condition | Test Method | CELANESE USA/211-45 |
|---|---|---|---|
| elongation | 断裂,23°C，横向 | ASTM D412 | 340 % |
| Tensile stress | 100%应变,23°C，横向流量 | ISO 37 | 1.40 Mpa |
| tensile strength | 断裂,23°C，横向流量 | ASTM D412 | 3.50 Mpa |
| elongation | 断裂,23°C，横向 | ISO 37 | 340 % |
| compression set | 23°C,22hr | ISO 815 | 11 % |
| tensile strength | Break,23°C | ISO 37 | 3.50 Mpa |
| compression set | 125°C,70hr | ISO 815 | 35 % |
| Tensile stress | 100%应变,23°C，横向流量 | ASTM D412 | 1.40 Mpa |
| compression set | 23°C,22hr | ASTM D395B | 11 % |
| 125°C,70hr | ASTM D395B | 35 % |
| aging | Test Condition | Test Method | CELANESE USA/211-45 |
|---|---|---|---|
| Change rate of tensile strength in air | 125°C,70hr,inIRM903Oil | ASTM D471 | -39 % |
| elongation at break | 125°C,70hr,inIRM903Oil | ASTM D471 | -54 % |
| Tensile strain change rate | 125°C,70hr,inIRM903Oil | ISO 1817 | -39 % |
| Change rate of elongation at break | 125°C,70hr,inIRM903Oil | ISO 1817 | -54 % |
| volume change | 125°C,70hr,在IRM903油中 | ASTM D471 | 120 % |
| Hardness change rate in the air | ShoreA,150°C,168hr | ASTM D573 | 1.0 |
| Change rate of ultimate elongation in air | 150°C,168hr | ASTM D573 | 26 % |
| Change rate of tensile strength in air | 150°C,168hr | ASTM D573 | -23 % |
| volume change | 125°C,70hr,在IRM903油中 | ISO 1817 | 120 % |
| Change rate of tensile strength in air | 150°C,168hr | ISO 188 | -23 % |
| Shore hardness | ShoreA,150°C,168hr | ISO 188 | 1.0 |
| Thermal performance | Test Condition | Test Method | CELANESE USA/211-45 |
|---|---|---|---|
| brittle temperature | ISO 812 | -62.0 °C | |
| RTI Str | 1.0mm | UL 746 | 90.0 °C |
| brittle temperature | ASTM D746 | -62.0 °C | |
| RTI Str | 3.0mm | UL 746 | 95.0 °C |
| RTI Elec | UL 746 | 100 °C |