PBT 2002U JAPAN POLYPLASTIC
DURANEX®
Electrical applications,Electronic and electrical components
Flame retardant,Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/2002U |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 90 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/2002U |
|---|---|---|---|
| ColorNumber | EF2001/ED3002 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/2002U |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 3.4 kJ/m² | |
| Nominal tensile fracture strain | ISO 527-2 | 100 % | |
| tensile strength | ISO 527-1/-2 | 60 Mpa | |
| bending strength | ISO 178 | 95 Mpa | |
| Flexural modulus | ISO 178 | 2630 Mpa | |
| tensile strength | ISO 527-2 | 60.0 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2002U |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 5E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 14 KV/mm |
| Volume resistivity | IEC 60093 | 5×1016 Ω.cm | |
| Surface Resistivity | IEC 60093 | 2×1017 Ω |
| other | Test Condition | Test Method | JAPAN POLYPLASTIC/2002U |
|---|---|---|---|
| characteristic | 非强化.一般.抗UV | ||
| Color | 本色 EF2001 | ||
| purpose | 注塑级 |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/2002U |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.9 % | |
| density | ASTM D792/ISO 1183 | 1.31 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.09 % |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/2002U |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/2002U |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2002U |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB/0.71 | |
| Linear coefficient of thermal expansion | 流动方向 | ISO 11359-2 | 10 ×10-5/℃ |
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 70 °C |
| Linear coefficient of thermal expansion | 垂直方向 | ISO 11359-2 | 10 ×10-5/℃ |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 70 ℃（℉） |
| Linear coefficient of thermal expansion | TD:23到55°C | 内部方法 | 1.1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C |
| Linear coefficient of thermal expansion | MD:23到55°C | 内部方法 | 1.1E-04 cm/cm/°C |
| UL flame retardant rating | UL 94 | HB |