PBT SK645FR NC010 DUPONT JAPAN
Crastin®
Electronic and electrical、Automotive Applications
Flame retardant、Glass fiber reinforced、Filler: Glass fiber reinf、20% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT JAPAN/SK645FR NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT JAPAN/SK645FR NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 8300 Mpa | |
| bending strength | ISO 178 | 165 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.8 % |
| tensile strength | 断裂 | ISO 527-2 | 110 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT JAPAN/SK645FR NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 |
| flammability | Test Condition | Test Method | DUPONT JAPAN/SK645FR NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| FMVSS flammability | FMVSS302 | DNI | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 32 % |
| physical property | Test Condition | Test Method | DUPONT JAPAN/SK645FR NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.2 % |
| MD | ISO 294-4 | 0.50 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.32 % |
| Ejection Temperature | 170 °C | ||
| Shrinkage rate | MD2 | ISO 294-4 | 0.60 % |
| TD2 | ISO 294-4 | 1.5 % | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.13 % |
| Thermal performance | Test Condition | Test Method | DUPONT JAPAN/SK645FR NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C |