Ethylene Copolymer Teflon® PFA 945HP Plus The Chemours Company
--
--
physical property
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | The Chemours Company/Teflon® PFA 945HP Plus | |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 600 MPa |
| Shore hardness | 邵氏D | ISO 868 | 55 |
| 邵氏D | ASTM D2240 | 55 | |
| elongation | 断裂,23°C | ASTM D3307 | 290 % |
| density | ASTM D792 | 2.14 g/cm³ | |
| Dissipation Factor | 1MHz | ASTM D150 | <2.0E-4 |
| Tensile strain | 断裂,200°C | ISO 12086 | 450 % |
| Volume resistivity | ISO 1325 | 1E+18 ohms·cm | |
| Flexural modulus | 23°C | ASTM D790 | 600 MPa |
| melt mass-flow rate | 372°C/5.0kg | ISO 12086 | 7.0 g/10min |
| tensile strength | 23°C | ASTM D3307 | 28.0 MPa |
| critical shear rate | 372°C | 21.0 sec^-1 | |
| Limiting Oxygen Index | ASTM D2863 | >95 % | |
| tensile strength | 200°C | ASTM D3307 | 13.0 MPa |
| 23°C | ISO 12086 | 28.0 MPa | |
| Dissipation Factor | 1MHz | IEC 60250 | <2.0E-4 |
| dielectric strength | 0.250mm | IEC 60243-1 | 80 kV/mm |
| Tensile strain | 断裂,23°C | ISO 12086 | 290 % |
| melting temperature | ASTM D4591 | 290 °C | |
| dielectric strength | 0.250mm | ASTM D149 | 80 kV/mm |
| Flexural modulus | 200°C | ISO 178 | 55.0 MPa |
| tensile strength | 200°C | ISO 12086 | 13.0 MPa |
| dielectric constant | 1MHz | ASTM D150 | 2.03 |
| melt mass-flow rate | 372°C/5.0kg | ASTM D3307 | 7.0 g/10min |
| Water absorption rate | 24hr | ASTM D570 | <0.030 % |
| UL flame retardant rating | UL 94 | V-0 | |
| elongation | 断裂,200°C | ASTM D3307 | 450 % |
| MITFoldingEndurance | 200.0µm | ASTM D2176 | 8E+05 Cycles |
| dielectric constant | 1MHz | IEC 60250 | 2.03 |
| Flexural modulus | 200°C | ASTM D790 | 55.0 MPa |
| Limiting Oxygen Index | ISO 4589-2 | >95 % | |
| Volume resistivity | ASTM D257 | 1E+18 ohms·cm |