Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 Vydyne® R515H BK02 美国奥升德（首诺）
--
汽车的发动机罩下的零件,构件,汽车领域的应用
填料,玻璃纤维增强材料,15%,填料按重量,
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 美国奥升德（首诺）/Vydyne® R515H BK02 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 6.0 kJ/m² |
| -30°C | ISO 179 | 6.0 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 6.6 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 32 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 5.7 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 39 kJ/m² |
| Electrical performance | Test Condition | Test Method | 美国奥升德（首诺）/Vydyne® R515H BK02 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 2 |
| dielectric strength | 1.00mm | IEC 60243 | 20 kV/mm |
| arc resistance | 3.00mm | ASTM D495 | PLC6 |
| Hot wire ignition (HWI) | 0.75mm | UL 746 | PLC 4 |
| 1.5mm | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| Volume resistivity | 0.750mm | IEC 60093 | 1E+13 ohms·cm |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 4 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 0 |
| 0.75mm | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | 美国奥升德（首诺）/Vydyne® R515H BK02 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 5900 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| Tensile modulus | 23°C | ISO 527-2 | 6600 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 120 MPa |
| Poisson's ratio | ISO 527-2 | 0.40 | |
| bending strength | 23°C | ISO 178 | 170 MPa |
| flammability | Test Condition | Test Method | 美国奥升德（首诺）/Vydyne® R515H BK02 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 675 °C |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 675 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 700 °C |
| 1.5mm | IEC 60695-2-13 | 700 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 675 °C |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 700 °C |
| physical property | Test Condition | Test Method | 美国奥升德（首诺）/Vydyne® R515H BK02 |
|---|---|---|---|
| Shrinkage rate | MD:23°C,2.00mm | ISO 294-4 | 0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.0 % |
| 平衡,23°C,50%RH | ISO 62 | 2.2 % | |
| density | ISO 1183 | 1.24 g/cm³ | |
| Shrinkage rate | TD:23°C,2.00mm | ISO 294-4 | 1.0 % |
| Thermal performance | Test Condition | Test Method | 美国奥升德（首诺）/Vydyne® R515H BK02 |
|---|---|---|---|
| RTI Str | 0.75mm | UL 746 | 125 °C |
| MD：23to55°C,2.00mm | ISO 11359-2 | 3E-05 cm/cm/°C | |
| RTI Imp | 1.5mm | UL 746 | 120 °C |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 241 °C |
| RTI Elec | 3.0mm | UL 746 | 140 °C |
| RTI Imp | 3.0mm | UL 746 | 120 °C |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 258 °C |
| TD：23to55°C,2.00mm | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| RTI Elec | 0.75mm | UL 746 | 140 °C |
| melting temperature | ISO 11357-3 | 260 °C | |
| RTI Imp | 0.75mm | UL 746 | 120 °C |
| RTI Str | 1.5mm | UL 746 | 140 °C |
| 3.0mm | UL 746 | 140 °C | |
| RTI Elec | 1.5mm | UL 746 | 140 °C |