| Impact resistance | Test Condition | Test Method | Canada Fiberfil/PP-60/TC/40 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 27 J/m |
| hardness | Test Condition | Test Method | Canada Fiberfil/PP-60/TC/40 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 90to95 |
| Mechanical properties | Test Condition | Test Method | Canada Fiberfil/PP-60/TC/40 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 48.3 MPa |
| tensile strength | 23°C | ASTM D638 | 31.0 MPa |
| Tensile modulus | 23°C | ASTM D638 | 3860 MPa |
| Flexural modulus | 23°C | ASTM D790 | 3650 MPa |
| elongation | 屈服,23°C | ASTM D638 | 10 % |
| physical property | Test Condition | Test Method | Canada Fiberfil/PP-60/TC/40 |
|---|---|---|---|
| Shrinkage rate | MD：6.35mm | ASTM D955 | 0.90 % |
| Water absorption rate | 24hr | ASTM D570 | 0.030 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 9.0 g/10min |
| density | ASTM D792 | 1.25 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.70 % |
| Thermal performance | Test Condition | Test Method | Canada Fiberfil/PP-60/TC/40 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 87.8 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 132 °C |