Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1800R SABIC INNOVATIVE US
LEXAN™
Casters、Automotive sector、Household appliances、Electronic field、Electrical field
High gloss、Aging resistance、wear resistant、Weather resistance、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1800R |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 124 °C | |
| ASTME831 | 7E-05 cm/cm/°C | ||
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 135 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 124 °C | |
| Vicat Softening Temperature | ISO527-3/1 | 141 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 135 °C | |
| ISO11359-2 | 7E-05 cm/cm/°C | ||
| Thermal Conductivity | DENKA Method | 0.20 W/m/K |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/1800R |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | ASTMD785 | 120 | |
| R-Scale | ISO2039-2 | 120 |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1800R |
|---|---|---|---|
| ASTMD638 | 2350 Mpa | ||
| fracture | ISO527-2/50 | >70 % | |
| Yield,50.0mm Span | ASTMD790 | 90.0 Mpa | |
| Break | ASTMD638 | >70 % | |
| yield | ISO527-2/50 | 6.0 % | |
| Yield | ASTMD638 | 6.0 % | |
| 50.0mm Span | ASTMD790 | 2300 Mpa | |
| ISO178 | 90.0 Mpa | ||
| Yield | ASTMD638 | 63.0 Mpa | |
| yield | ISO527-2/50 | 63.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/1800R |
|---|---|---|---|
| Saturation ,23℃ | ASTMD570 | 0.35 % | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50到0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 18 g/10min |
| Saturation ,23℃ | ISO62 | 0.35 % | |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 17.0 cm3/10min |
| Modeling Shrinkage | MD：--1 | 内部方法 | 0.50到0.70 % |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/1800R |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 88.0到90.0 % |
| Index of Refraction | ASTMD542,ISO489 | 1.586 | |
| Haze | 2540µm | ASTMD1003 | <0.80 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1800R |
|---|---|---|---|
| ASTMD256 | 700 J/m | ||
| ISO180/1A | 70 kJ/m² | ||
| ASTMD4812,ISO180/1U | 无断裂 | ||
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 65.0 J |
| ISO180/1U | 无断裂 |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/1800R |
|---|---|---|---|
| Flame Rating | 1.50mm | UL94 | V-2 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1800R |
|---|---|---|---|
| Dielectric Strength | 1.60mm | ASTMD2863 | 27 KV/mm |
| Dielectric Constant | 1MHz | ASTMD150,IEC60250 | 3.00 |
| 60Hz | ASTMD150,IEC60250 | 3.00 | |
| Dissipation Factor? | 1MHz | ASTMD150,IEC60250 | 0.010 |
| Volume Resistivity | ASTMD257,IEC60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor? | 60Hz | ASTMD150,IEC60250 | 1E-03 |