PBT VX5022-7001 SABIC INNOVATIVE US
VALOX™ 
engineering application ,Automotive components,Electronic and electrical components
High mobility,High crystallinity,Aging resistance,Filler: Glass fiber reinf,20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-7001
-30°CISO 179/2C9.0 kJ/m²
23°CISO 180/1A7.0 kJ/m²
Dart impact23°C,TotalEnergyASTM D376365.0 J
23°CISO 179/1eU40 kJ/m²
-30°CASTM D25680 J/m
ISO 179/1eA5.5 kJ/m²
ASTM D4812650 J/m
ISO 179/1eU40 kJ/m²
ISO 179/2U50 kJ/m²
23°CISO 179/1eA6.5 kJ/m²
0°CASTM D25680 J/m
23°CISO 180/1U40 kJ/m²
ASTM D25680 J/m
ISO 179/2C9.0 kJ/m²
ASTM D4812650 J/m
-30°CISO 180/1A6.0 kJ/m²
0°CISO 180/1A7.0 kJ/m²
-30°CISO 180/1U35 kJ/m²
23°CISO 179/2U55 kJ/m²
Supplementary InformationTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-7001
fillerASTM D22920 %
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-7001
Rockwell hardnessR计秤ISO 2039-2122
ball-indentation hardnessH358/30ISO 2039-1205 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-7001
1.60mm, In oilIEC 60243-128 KV/mm
Volume resistivityASTMD257>1.0E+15 ohms·cm
High arc combustion index (HAI)HAIUL 746PLC 0
3.20mm, In oilIEC 60243-116 KV/mm
60Hz60HzIEC 602501E-03
50Hz50HzIEC 602503.10
Compared to the Leakage Tracking Index (CTI)解决方案BIEC 60112PLC 4
--IEC 60112PLC 3
0.800mm, In oilIEC 60243-131 KV/mm
0.800mm, inoilASTM D14931 KV/mm
100Hz100HzIEC 602501E-03
Hot wire ignition (HWI)HWIUL 746PLC 0
16mm, inoylASTM D14928 KV/mm
Surface ResistivityIEC 60093>1.0E+15 ohms
3.20mm, inoilASTM D14916 KV/mm
1MHz1MHzASTMD1503.30
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-7001
yieldASTM D6383.0 %
ASTM D638125 Mpa
fractureISO 527-2/5110 Mpa
Yield, 50.0mm spanASTM D790145 Mpa
--3ASTM D6387300 Mpa
yieldISO 527-2/5110 Mpa
ISO 527-2/53.0 %
fractureASTM D638125 Mpa
--10ISO 178150 Mpa
fractureASTM D6383.0 %
--9ISO 1786300 Mpa
50.0mm spanASTM D7905800 Mpa
Fracture bending strainISO 1783.0 %
fractureISO 527-2/53.0 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-7001
Burning wire flammability index2.00mmIEC 60695-2-12850 °C
UL flame retardant rating1.60mmUL 94HB
Burning wire flammability index1.00mmIEC 60695-2-12750 °C
Limiting Oxygen IndexISO 4589-223 %
Filling analysisTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-7001
melt viscosity260°C,1500sec^-1ISO 11443215 Pa·s
physical property Test ConditionTest MethodSABIC INNOVATIVE US/VX5022-7001
melt mass-flow rate250°C/2.16kgASTM D123816 g/10min
265°C/5.0kgASTM D123850 g/10min
Shrinkage rateTD2内部方法0.50-0.90 %
MD:3.20mm内部方法0.30-0.50 %
densityASTMD7921.39 g/cm³
melt mass-flow rate266°C/5.0kgASTM D123850 g/10min
Melt volume flow rate250°C/5.0kgISO 113328.0 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.060 %
饱和,23°CISO 620.10 %
Melt volume flow rate265°C/5.0kgISO 113340.0 cm3/10min
Shrinkage rateMD1内部方法0.30-0.80 %
Melt volume flow rate250°C/2.16kgISO 113313.0 cm3/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-7001
Flow: 23 to 60 ° C23到60℃ISO 11359-24E-05 cm/cm/°C
Horizontal: 23 to 80 ° C横向, 23到80℃ISO 11359-21E-04 cm/cm/°C
Flow: -40 to 40 ° CASTME8314E-05 cm/cm/°C
ISO 11359-22.5E-05 cm/cm/°C
Flow: 23 to 150 ° C23到150℃ISO 11359-22.4E-05 cm/cm/°C
0.45MPa, Unanealed, 3.20mmASTM D648180 °C
Horizontal: 23 to 150 ° C横向, 23到150℃ISO 11359-21.1E-04 cm/cm/°C
Flow: 23 to 80 ° C23到80℃ISO 11359-24E-05 cm/cm/°C
Horizontal: -40 to 40 ° C横向, -40到40℃ISO 11359-26.9E-05 cm/cm/°C
横向, -40到40℃ASTME8311E-04 cm/cm/°C
0.45MPa, Unanealed, 64.0mm spanISO 75-2/Bf180 °C
1.8MPa, Unanealed, 64.0mm spanISO 75-2/Af120 °C
1.8MPa, Unanealed, 3.20mmASTM D648120 °C
Horizontal: 23 to 60 ° C横向, 23到60℃ISO 11359-21E-04 cm/cm/°C
ball-indentation hardness125°CIEC 60695-10-2Pass