Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 13G50 ASAHI JAPAN
Leona™ 
Electrical applications,Automotive Applications,Gears
Fatigue resistance,High rigidity,Creep resistance,high strength
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodASAHI JAPAN/13G50
Impact strength of simply supported beam without notchISO 179无断裂
hardnessTest ConditionTest MethodASAHI JAPAN/13G50
Rockwell hardnessM 级ASTM D78595
M 计秤ISO 2039-295
R 计秤ISO 2039-2118
R 级ASTM D785118
Mechanical propertiesTest ConditionTest MethodASAHI JAPAN/13G50
tensile strength 断裂, 23°CISO 527-2237 Mpa
Taber abraser1000 CyclesASTM D1044-- mg
elongation断裂ASTM D6382.5 %
tensile strength --ASTM D638235 Mpa
elongation断裂, 23°CISO 527-22.0 %
bending strength--ASTM D790390 Mpa
23°CISO 178371 Mpa
Flexural modulus23°CISO 17813600 Mpa
Tensile modulus23°CISO 527-216900 Mpa
Flexural modulus--ASTM D79014500 Mpa
Electrical performanceTest ConditionTest MethodASAHI JAPAN/13G50
Compared to the Leakage Tracking Index (CTI)3.00 mmIEC 60112 V
Surface ResistivityASTM D2571.0E+15 ohms
Volume resistivity--ASTM D2571.0E+15 ohms·cm
23°CIEC 600931.0E+15 ohms·cm
dielectric strengthASTM D14921 KV/mm
flammabilityTest ConditionTest MethodASAHI JAPAN/13G50
UL flame retardant rating0.75 mmUL 94HB
physical property Test ConditionTest MethodASAHI JAPAN/13G50
Water absorption rate平衡, 23°C, 50% RHISO 62-- %
Shrinkage rate横向流量内部方法0.70 %
Water absorption rate饱和, 23°C-- %
Shrinkage rate流量内部方法0.40 %
Thermal performanceTest ConditionTest MethodASAHI JAPAN/13G50
thermal conductivity0.40 W/m/K
Heat distortion temperature0.45 MPa, 未退火，HDTASTM D648260 °C
1.8 MPa, 未退火，HDTISO 75-2/A255 °C
1.8 MPa, 未退火，HDTASTM D648250 °C
Linear coefficient of thermal expansion流动ASTM D6962.0E-5 cm/cm/°C