PC 4019 SABIC INNOVATIVE US
LEXAN™
Lighting applications、Plastic bag
Middle flow、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4019 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 135 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/B50 | 146 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 4.7E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 137 °C |
| Vicat Softening Temperature | ASTMD152510 | 146 °C | |
| -- | ISO306/B120 | 146 °C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 4.7E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/4019 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.40 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.20to0.60 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 7.5 g/10min |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.20to0.60 % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 6.50 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.15 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4019 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 3500 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 14 % |
| Tensile Strain | 断裂 | ISO527-2/5 | 8.7 % |
| Tensile Modulus | ISO527-2/1 | 3900 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 55.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 48.0 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 103 Mpa |
| Flexural Modulus | ISO178 | 3450 Mpa | |
| Tensile Elongation | 屈服 | ASTMD638 | 4.3 % |
| Flexural Strength | ISO178 | 98.0 Mpa | |
| Tensile Modulus | ASTMD638 | 3950 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 45.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/5 | 4.3 % |
| Tensile Stress | 屈服 | ISO527-2/5 | 54.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4019 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 15 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 40.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 25 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | NoBreak |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 25 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/4019 |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | HB |