Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA XTWE270M BR1D182 SABIC INNOVATIVE US
GELOY™
Automotive Applications、Electrical applications
Thermal stability、Antistatic、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/XTWE270M BR1D182 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 28.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| 23°C | ISO 180/1A | 13 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/XTWE270M BR1D182 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1790 Mpa | |
| elongation | 屈服 | ASTM D638 | 3.4 % |
| tensile strength | 断裂 | ASTM D638 | 32.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 3.4 % |
| tensile strength | 断裂 | ISO 527-2/50 | 26.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1830 Mpa |
| Tensile modulus | ASTM D638 | 1910 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 36.0 Mpa |
| elongation | 断裂 | ASTM D638 | 38 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 56.0 Mpa |
| ISO 178 | 56.0 Mpa | ||
| Flexural modulus | ISO 178 | 1870 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 36.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 28 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/XTWE270M BR1D182 |
|---|---|---|---|
| Melt volume flow rate | 220°C/5.0kg | ISO 1133 | 2.00 cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.30-0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.80 % | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 9.7 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/XTWE270M BR1D182 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 85.0 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 82.0 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 9.2E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| vicat | ASTM D152510 | 85.0 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 71.0 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 69.0 °C |