ABS Reblend® 6520/OP NERO SO.F.TER ITALY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SO.F.TER ITALY/Reblend® 6520/OP NERO |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 550 J/m |
| Mechanical properties | Test Condition | Test Method | SO.F.TER ITALY/Reblend® 6520/OP NERO |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 50 % |
| Tensile modulus | ASTM D638 | 2400 MPa | |
| tensile strength | 断裂 | ASTM D638 | 45.0 MPa |
| Flexural modulus | ASTM D790 | 2600 MPa | |
| tensile strength | 屈服 | ASTM D638 | 50.0 MPa |
| bending strength | ASTM D790 | 90.0 MPa |
| Electrical performance | Test Condition | Test Method | SO.F.TER ITALY/Reblend® 6520/OP NERO |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| Volume resistivity | 23°C | ASTM D257 | 1E+15 ohms·cm |
| flammability | Test Condition | Test Method | SO.F.TER ITALY/Reblend® 6520/OP NERO |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SO.F.TER ITALY/Reblend® 6520/OP NERO |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.65 % | |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 24 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.70 % |
| density | ASTM D792 | 1.12 g/cm³ |
| Thermal performance | Test Condition | Test Method | SO.F.TER ITALY/Reblend® 6520/OP NERO |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 101 °C |
| vicat | -- | ASTM D15252 | 130 °C |
| -- | ASTM D15253 | 120 °C |