PC/PBT 508-1001 SABIC INNOVATIVE US
XENOY™
Household daily necessiti、Electrical applications、Automotive Applications
Chemical resistance、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/508-1001 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 640 J/m |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 8.00 J |
| 23°C, Energy at Peak | ASTM D3763 | 6.00 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/508-1001 |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 119 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/508-1001 |
|---|---|---|---|
| bending strength | 断裂, 50.0 mm 跨距 | ASTM D790 | 189 Mpa |
| tensile strength | 断裂 | ASTM D638 | 110 Mpa |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 6890 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/508-1001 |
|---|---|---|---|
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 29 KV/mm |
| Volume resistivity | ASTM D257 | 5.9E+16 ohms·cm | |
| Dissipation Factor | 100 Hz | ASTM D150 | 1.4E-3 |
| dielectric constant | 100 Hz | ASTM D150 | 3.60 |
| 1 MHz | ASTM D150 | 3.60 | |
| Hot wire ignition (HWI) | UL 746 | PLC 1 | |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 24 KV/mm |
| arc resistance | ASTM D495 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.020 |
| High arc combustion index (HAI) | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/508-1001 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/508-1001 |
|---|---|---|---|
| Shrinkage rate | 横向流动 : 3.20 到 4.60 mm | 内部方法 | 0.60 - 0.90 % |
| 流动 : 1.50 到 3.20 mm | 内部方法 | 0.30 - 0.50 % | |
| 横向流动 : 1.50 到 3.20 mm | 内部方法 | 0.40 - 0.60 % | |
| Outdoor applicability | UL 746C | f2 | |
| Water absorption rate | 24 hr | ASTM D570 | 0.060 % |
| Specific volume | ASTM D792 | 0.660 cm³/g | |
| Shrinkage rate | 流动 : 3.20 到 4.60 mm | 内部方法 | 0.50 - 0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/508-1001 |
|---|---|---|---|
| Linear coefficient of thermal expansion | -40 到 40°C，流动 | ASTM E831 | 2.3E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 176 °C |
| RTI Imp | UL 746 | 110 °C | |
| RTI | UL 746 | 125 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 215 °C |
| Linear coefficient of thermal expansion | 60 到 138°C，流动 | ASTM E831 | 1.6E-5 cm/cm/°C |
| RTI Elec | UL 746 | 125 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/508-1001 |
|---|---|---|---|
| screw speed | 50 to 80 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 250 to 265 °C | ||
| drying temperature | 120 °C | ||
| Suggested injection volume | 40 to 80 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 245 to 260 °C | ||
| Temperature at the rear of the barrel | 240 to 255 °C | ||
| Exhaust hole depth | 0.025 to 0.038 mm | ||
| Temperature at the front of the material cylinder | 250 to 265 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 65 to 90 °C | ||
| Spray nozzle temperature | 245 to 260 °C |