Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO(PPE)+PP LEMALLOY® PX603Y Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/LEMALLOY® PX603Y |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/LEMALLOY® PX603Y |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 1900 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 1900 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 42.0 MPa |
| bending strength | 23°C | ISO 178 | 59.0 MPa |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/LEMALLOY® PX603Y |
|---|---|---|---|
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 55.0 cm³/10min |
| Shrinkage rate | TD:3.20mm | 1.1to1.3 % | |
| MD:3.20mm | 1.0to1.2 % | ||
| density | ISO 1183 | 0.980 g/cm³ |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/LEMALLOY® PX603Y |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 120 °C |