Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PPA A-1133 WH505 SOLVAY USA

AMODEL®

Shell、Vehicle electronics、Phone、Industrial components、Automotive interior parts、Industrial applications、Metal substitution、Fuel pipeline、Machine/mechanical compon、Application in the automo、Power/Other Tools、Laptop case、Parts under the hood of a

Chemical resistance、Low moisture absorption、Filler: Glass fiber reinf、33% filler by weight

Plastic Datasheets

Mechanical properties	Test Condition	Test Method	SOLVAY USA/A-1133 WH505
bending strength	23°C	ISO 178	319 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.5 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.8 kJ/m²
Flexural modulus	23°C	ISO 178	11600 Mpa
Tensile modulus	23°C	ISO 527-2	13400 Mpa
elongation at break	23°C	ISO 527-2	2.5 %
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	49 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	73 kJ/m²
tensile strength	23°C	ISO 527-2	233 Mpa

Electrical performance	Test Condition	Test Method	SOLVAY USA/A-1133 WH505
dielectric strength	3.20mm	IEC 60243-1	39 KV/mm
Volume resistivity		IEC 60093	1E+15 Ω.cm

Flame retardant performance	Test Method	SOLVAY USA/A-1133 WH505
UL flame retardant rating	UL -94	HB 1.5mm
		UL -94	HB 3.0mm
		UL -94	HB 0.84mm

physical property	Test Condition	Test Method	SOLVAY USA/A-1133 WH505
density		ISO 1183	1.48 g/cm³

Thermal performance	Test Condition	Test Method	SOLVAY USA/A-1133 WH505
Heat distortion temperature	1.80MPa退火，HDT	ISO 75-2/Af	280 °C
vicat	熔融温度	ISO 11357-3	313 °C