TPO PRE-ELEC® PP 1380 Premix Oy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1380
Charpy Notched Impact Strength-20°CASTM D2562.1 kJ/m²
Impact strength of cantilever beam gap23°CISO 1803.0 kJ/m²
Impact strength of simply supported beam without notch-20°CASTM D25663 kJ/m²
Charpy Notched Impact Strength23°CASTM D2566.3 kJ/m²
Impact strength of cantilever beam gap-20°CISO 1802.0 kJ/m²
Suspended wall beam without notch impact strength-20°CISO 18013 kJ/m²
Impact strength of simply supported beam without notch23°CASTM D256NoBreak
Charpy Notched Impact Strength23°CISO 1798.0 kJ/m²
Suspended wall beam without notch impact strength23°CISO 18049 kJ/m²
-20°C,4.00mmASTM D25612.6 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Impact strength of cantilever beam gap-20°C,4.00mm，AreaASTM D2562.10 kJ/m²
23°C,4.00mm，AreaASTM D2562.10 kJ/m²
Impact strength of simply supported beam without notch-20°CISO 17961 kJ/m²
Suspended wall beam without notch impact strength23°C,4.00mmASTM D25648.3 kJ/m²
Charpy Notched Impact Strength-20°CISO 1793.0 kJ/m²
hardnessTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1380
Shore hardness邵氏DASTM D224072
邵氏DISO 86872
邵氏AISO 86897
邵氏AASTM D224097
Mechanical propertiesTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1380
tensile strength ASTM D63826.2 MPa
Tensile strain断裂,4.00mmISO 527-25.0 %
Flexural modulus4.00mmASTM D7901930 MPa
4.00mmISO 1781900 MPa
tensile strength 4.00mmISO 527-226.0 MPa
Electrical performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1380
Surface ResistivityESDSTM11.11<1.0E+2 ohms
IEC 61340-2-3<1.0E+2 ohms
Volume resistivity内部方法<5.0 ohms·cm
physical property Test ConditionTest MethodPremix Oy/PRE-ELEC® PP 1380
melt mass-flow rate230°C/5.0kgASTM D12381.5 g/10min
Shrinkage rateMDASTM D9551.2to1.7 %
MDISO 294-41.2to1.7 %
densityASTM D7921.05 g/cm³
ISO 11831.06 g/cm³
melt mass-flow rate230°C/5.0kgISO 11331.5 g/10min
Thermal performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1380
Heat distortion temperature1.8MPa,未退火，HDTASTM D648A57.8 °C
1.8MPa,未退火，HDTISO 75-2/Af58.0 °C
0.45MPa,未退火，HDTASTM D648B104 °C
vicat--ISO 306/A50150 °C
--ASTM D15253150 °C
--ASTM D1525480.0 °C
--ISO 306/B5080.0 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/Bf104 °C