PBT Lupox® HI2100M LG Chem Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./Lupox® HI2100M |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 34 J/m |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./Lupox® HI2100M |
|---|---|---|---|
| bending strength | 屈服,3.20mm | ASTM D790 | 98.1 MPa |
| elongation | 断裂,3.20mm | ASTM D638 | 4.0 % |
| tensile strength | Break,3.20mm | ASTM D638 | 68.6 MPa |
| Flexural modulus | 3.20mm | ASTM D790 | 3140 MPa |
| physical property | Test Condition | Test Method | LG Chem Ltd./Lupox® HI2100M |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 26 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.70to1.1 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.070 % |
| density | ASTM D792 | 1.37 g/cm³ |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./Lupox® HI2100M |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 190 °C |
| melting temperature | ASTM D3418 | 223 °C |