Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT BM6450XD BK560 DUPONT USA
Cristin®
Blow molding applications
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| thermal performance | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 50.0 °C |
| 0.45 Mpa，未退火（Flatwise），HDT | ISO 75B-1 | 130 ℃ | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 80.0 °C | |
| 0.45MPa,退火，HDT | ISO 75-2/B | 130 °C | |
| melting temperature | ISO 11357-3 | 220 °C |
| Electrical performance | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 31 KV/mm | |
| Dissipation Factor | 100Hz | IEC 60250 | 7E-03 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 50 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 1600 Mpa | |
| Impact strength of simply supported beam without notch | 23 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Tensile strain | 屈服 | ISO 527-2 | 9.0 % |
| Impact strength of simply supported beam without notch | -30 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Tensile modulus | 23 ℃, 1.0 mm/min | ISO 527-1 | 1600 MPa |
| elongation | 23 °C, 50 mm/min，屈服 | ISO 527-1 | 9.3 % |
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| Tensile stress | 23 ℃, 50 mm/min，屈服 | ISO 527-1 | 34 MPa |
| tensile strength | 屈服 | ISO 527-2 | 34.0 Mpa |
| bending strength | ISO 178 | 50.0 Mpa | |
| flexural modulus | ISO 178 | 1600 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 1600 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | 23℃, 2 mm/min | ISO 178 | 1600 MPa |
| ASTM D790/ISO 178 | 1600 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| characteristic | 可加工性良好 耐化学性良好 | ||
| purpose | 吹塑成型应用 |
| Physical properties | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| ThermalConductivityofMelt | 0.15 W/m/K | ||
| SpecificHeatCapacity of Melt | 2210 J/kg/°C | ||
| density | ASTM D792/ISO 1183 | 1.21 | |
| shrinkage rate | TD | ISO 294-4 | 1.7 % |
| MediumDensity | 1.03 g/cm³ | ||
| shrinkage rate | MD | ISO 294-4 | 1.5 % |
| flammability | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| burning rate | 1.00mm | ISO 3795 | 40 mm/min |
| processability | Test Condition | Test Method | DUPONT USA/BM6450XD BK560 |
|---|---|---|---|
| mold temperature | 30-130 °C |